Abstract
Pellet type $Pt/MoO_{3}$ gas sensor which is operating at much lower temperature than conventional ceramic sensors such as $SnO_{2}$ or ZnO was fabricated. Morphology and crystal structure of $Pt/MoO_{3}$ according to calcination temperature have been characterized with Transmission Electron microscopy and X-Ray powder diffraction. The characterization indicates that as calcination temperature is increased, overlayers of $MoO_{3}$ on Pt are produced, but additionally, the Cl content associated with the Pt phase diminishes. The gas dasorption test showed that the change in surface morphology is closely related to hydrogen storage capacity of the sample. The gas sensitivities at $50^{\circ}C$ and $150^{\circ}C$ are very high.
$300^{\circ}C$ 이상의 고온에서 동작하는 전통적인 $SnO_{2}$ 또는 ZnO와 같은 전통적인 세라믹 가스 센서보다 훨씬 낮은 온도에서 동작이 가능한 $Pt/MoO_{3}$ 가스 센서를 pellet 형으로 제작하였다. $Pt/MoO_{3}$ 가스 센서의 하고 온도(calcination temperature)에 따른 표면구조의 변화와 결정구조의 변화가 투과전자현미경(transmission electron microscopy)과 X-선 회절시험에 의하여 조사되었다. 투과전자현미경 사진으로부터 하소 온도가 증가할수록 시편에서 $PtCl_{x}$에서 Cl의 양이 줄어드는 것과 Pt위에 $MoO_{3}$의 얇은 막(overlayer)이 형성되어 있다는 것을 보여준다. 가스 흡착 시험 결과 표면구조의 변화에 따라서 시편의 수소 저장 능력이 변화함을 보여주었다. $50^{\circ}C$와 $150^{\circ}C$에서 수소가스 감지도를 측정한 결과 매우 우수한 결과를 보여 주었다.