Effect of Cosubstrate on tile Production of Poly(3-Hydroxybutyric-Co-3-Hydroxyvaleric) Acid from Glucose by Pseudomonas sp, HJ

Pseudomonas sp. HJ에 의한 포도당으로부터 Poly(3-Hydroxybutyric-Co-3-Hydroxyvaleric) Acid의 생합성에 대한 보조기질의 영향

Poly(3-hydroxybutyric-co-3-hydroxyvaleric) acid(PHB/HV) copolymer synthesis by Pseudomonas sp. HJ from glucose and cosubstrate was investigated. Taxonomic analysis suggested that Pseudomonas sp. HJ was best marched to Pseudomonas picketti having 78.8% similarity. Pseudomonas sp. HJ produced PHB/HV copolymer containing 60.8 mol% HV and 44.9 mol% HV when supplied with hexadecane and propionic acid as a cosubstrate, respectively. The HV composition in PHB/HV copolymer was controlled by varying the concentration of hexadecane and propionic acid. Propionic acid added after 24 hours of incubation was incorporated as the HV monomer in the PHB/HV copolymer up to 49.6 mol%.

본 연구에서는 단일 탄소원인 포도당으로부터 P PHA를 생산하는 콩시균 Pseudomonas sp. HJ를 보다 정확하게 동정하기 위하여 수치분류를 실시하 였으며, 또한 보조기질을 첨가하였을때의 PHB/HV 합성 양상을 검토하였다. Pseudomonas sp. HJ는 각 대조균주들중에서 Pseudomonas picketti와 가장 유 사도가 높은 것으로 나타났다(78.8%). 그러나 수치 분류에 서 통일 균종에 포함될 수 있는 유샤도는 85 % 정도인 것으로 얄려져 있으므로, 본 공시균 P Pseudomonas sp. HJ는 Pseudomonas 속의 다른 종 (species)이거나 새로운 종(species)일 가능성이 높 았다. 보조기 질로 hexadecane과 propionic acid를 각각 0.4%씩 첨가했을 경우, 농도증가에 비례하여 H HV 함량은 점차 증가하여 각각 60.8 mol%, 44.9 mol%까지 축적되었다. PHB/HV내의 HV 함량은 p propionic acid냐 hexadecane의 농도를 달리하여 첨가함으로써 조절할 수 있었다. 보조기질로 propl- onic acid 0.2 %를 대수기 중기 인 배양 18시간에 첨 가하였을때 균체 생육이 가장 우수하였으나, HV monomer의 비율은 대수기 말기인 배양 24시간대에 첨가하였을때 49.6 mol%로 가장 높았다.