Mechanical Properties of $Al_2O_3-AlN$ Particulate Composite

$Al_2O_3-AlN$계 입자복합체의 기계적 성질

  • 김영우 (부산대학교 무기재료공학과) ;
  • 박홍채 (부산대학교 무기재료공학과) ;
  • 오기동 (부산대학교 무기재료공학과)
  • Published : 1996.01.01
Download PDF
⟨ Previous Next ⟩

Abstract

The mechanical propertieso f sintered AlN with the addition of alumina were investigated The flexural strength of the AlN dispersed ALON specimens was higher than that of ALON and fracture toughness showed similar tendency. The high-temperature flexural strength of specimens which 50 and 64.3 mol% alumina was added to AlN was constant up to 100$0^{\circ}C$ with about 290 and 420 MPa respectively but abruptly decreased at 120$0^{\circ}C$ In the specimens which contained 5 and 30mol% alumina the flexural strength increased to about 14% at 100$0^{\circ}C$ and did not decrease at 120$0^{\circ}C$ compared to at room temperature.

Keywords

References

  1. Yogyo-Kyokai-Shi v.89 no.6 Effect of VArious Additives on Sintering of Aluminum Nitride K. Komeya;H. Inoue;A. Tsuge
  2. J Am. Ceram Soc. v.61 no.9-10 Effect of Oxygen Composition on Flexural Strength of Hot-Pressed AIN T.Sakai
  3. Rev. Int. Hautes Temp. Refract v.1 no.1 Formation at High Temperature of Nonstoichiometric Spinels and of Derived Phases in Several Oxide Systems Based on Alumina-Aluminum Nitride A. Lejus
  4. J. Am Ceram Soc. v.61 no.7-8 A Simple Model for Aluminum Oxynitride Spinels J W McCauley
  5. J. Ceram. Soc.Jpn Inter Edn. v.97 Fabrication of Translucent Sintered Aluminum Oxynitride Spinel (ALON) H. Takebe;T. Kameda;M. Komeya;K. Morinaga
  6. Bull Chem. Soc. Jpn. v.23 On the Refractive Power of the Lower Valent Al Ion (Al­ or Al+¹) in the Crystal G. Yamaguchi
  7. J. Eur Ceram Soc. v.10 Thermodynamics of AlonⅡ:Phase Relations H.X. Willems;M.M.R.M. Hendrix;G. de With;R. Metselaar
  8. J Am. Ceram. Soc. v.62 no.9-10 Phase Relations and Reaction Sintering of Transparent Cubic Aluminum Oxynitride Spinel (ALON) J.W. McCauley;N.D. Corbin
  9. J. Mat. Sci. v.10 Equilibrium Penny-like Cracks in Indentation Fracture B.R. Lawn;E.R. Fuller
  10. Am. Ceram Soc Bull. v.61 no.5 Thermomechanical Properties of Aluminum Oxynitride Spinel G.D. Qunn;N.D. Corbin;J.W. McCauley
  11. Nitrogen Ceramics Presentation of Multicomponent Silicon Nitride Based Systems L.J. Gauckler;G. Pelzow;F.L. Riley(ed.)
  12. Progress in Nitrogen Ceramics High Temperarture Reactions and Microstructures in the Al₂O₃-AIN System J W. McCauley;N.D. Corbin;F.L. Riley(ed.)
  13. Rev. Int Hautes Temp. Refract. v.13 Physical and Mechanical Properties of AIN-Al₂O₃Ceramic Bodies Prepared by Hot-Pressing R Kieffer;W. Wruss;B. Willer
  14. Proc. SPIE Int. Soc. Opt. Eng. v.297 Nitrogen-Stabilized Aluminum Oxide Spinel N.D. Corbin;J.W. McCauley
  15. J. Mat. Sci. v.28 Mechanical Properties of γ-Aluminum Oxynitride H.X. Willems;P.F. VanHal;G. de With;R. Metselaar
  16. Progress in Nitrogen Ceramics Sintering of Aluminum Nitride with Low Oxide Addition K.A. Schwetz;H. Knoch;A. Lipp;F.L. Riley(ed.)
  17. J. Am. Ceram. Soc. v.72 no.3 Effects of CaO on the Strength and Toughness of AIN S.R. Witek;G.A. Miller;M.P. Harner
  18. Ceram Eng. and Sci. Proc. v.3 Aluminum Oxynitride Spinel (ALON)-A New Optical and Multimode Window Material T.M. Hartnett;E.A. Maguire;R.L. Gentilman;N.D. Corbin;J.W. McCauley
  19. Sintering-Theory and Practice Hot-Pressed Oxynitride in the System AIN-Al₂O₃ T. Sakai;D. Kolar(ed.);S. Pejovnik(ed.)M.M. Ristic(ed.)