Abstract
It is very important to understand the domain structures of ferroelectric BaTiO3 in the poling process. Especially because {111} twinning is frequently observed in most BaTiO3 ceramics it is required to know the relations between the ferroelectric domains and the structural twin. In this study the domain structures of a {111} twinned crystal sample were observed under a polarizing microscope. and the relation between the {111} twin and the domain configurations could be classified into two types of 'V'-shape and linear shape penetrating perpendicular to the twin boundary. Domain formation obeys the symmetry of the {111} twining when a new domain structure is developed by heat treatment and surface deformation due to domain formation is also occured symmetrically between the both sides of the{111} twin boundary. This symmetrical behavior of the domains could be interpreted with the "head-to-tall" orientation of the domains across the {111} twin boundary.
강유전성 BaTiO3의 분역 구조를 이해하는 것은 폴링과정에 있어서 대단히 중요하면 대부분의 BaTiO3 세라믹스에서 흔히 발견되는 구조 쌍정 계면에서의 배향관계는 아직까지 보고된 바 없다. 본 연구에서는 {111} 쌍정을 이루고 있는 길정시편을 이용하여 편광현미경하에서 분역구조를 관찰하고, 열처리에 의하여 상전이되는 동안 {111} 쌍정과 강유전성 분역의 거동을 현미경하에서 직접적으로 관찰하였다. {111} 쌍정면 암측으로 대칭적 분역구조가 발될되며, 그 배열 형태는 'V'자 모양과 수직하게 관통하는 것처럼 직선 모양의 두가지 형으로 분류된다. 열처리에 의하여 새로운 분역구조가 형성될때 {111} 쌍정면 주위에서는 대칭적 관계를 유지하면서 분역이 발달되며, 분역형성에 기인하는 표면변형도 {111} 쌍정에 대하여 항상 대칭적으로 발달된다. 이는 {111} 계면에서도 분극반향이 바뀌어지며 "머리-꼬리"의 전지적 안정성의 배향관계를 유지하는 것으로 설명할 수 있다.