Abstract
The effect of AlN on the thermal conductivity of aluminum oxide pressurelessly sintered at nitrogen atmos-phere was investigated. Increasing aluminium nitride content up to 1~10 mol% the thermal conductivity of $Al_{2}O_{3}$-AlN system was singnificantly decreased and was constant with adding 20 and 25 mol% aluminium nitride. The thermal conuctivity of $Al_{2}O_{3}$ containing 1~10 mol% the thermal conductivity of $Al_{2}O_{3}$-AlN system was singificantly decreased and was constant with adding 20 and 25mol% aluminum nitride. The thermal conctivity of $Al_{2}O_{3}$ containing 1~10 mol% AlN showed a maximum at $1700^{\circ}C$ and decrea-sed with increasing sintering tempertures. This phenomenon was attributed to $\alpha$-$Al_{2}O_{3}$ and ALON formed by reacting $Al_{2}O_{3}$ with AlN up to $1700^{\circ}C$ and the secondary phases such as ${\gamma}$-ALON ($9Al_{2}O_{3}$.AlN)and $\Phi$($5Al_{2}O_{3}$.AlN) phase above $1750^{\circ}C$ The thermal conductivity of $Al_{2}O_{3}$ containing 20 and 25 mol% AlN showed maximum value at $1800^{\circ}C$ Both $\alpha$-$Al_{2}O_{3}$ and ALON existed up to $1600^{\circ}C$ value at $1800^{\circ}C$ Both $\alpha$-$Al_{2}O_{3}$ and ALON existed up to $1600^{\circ}C$ while only AlON phase existed above $1650^{\circ}C$.
질소 분위기에서 상압소결한 알루미나 소결체의 열전도도에 대한 AIN 첨가효과를 검토하였다. AIN 함량이 1,5 및 10 mol%롤 증가하면 $Al_{2}O_{3}$-AIN 소결체의 열전도도는 급격히 감소하지만, 20 및 25 mol%가 첨가되면 거의 일정하였다. 1~10mol% AIN이 첨가된 알루미나 소결체의 열전도도는 $1700^{\circ}C$의 소결온도에서 최대값을 나타내었으며, 소결온도가 $1800^{\circ}C$로 증가하면 감소하는 경향을 보였다. 이러한 현상은 $1700^{\circ}C$까지는 $\alpha$-$Al_{2}O_{3}$ 및 $Al_{2}O_{3}$와 AIN이 반응하여 생성되 ALON상이 존재하나, $1750^{\circ}C$부터 ${\gamma}$-ALON($9Al_{2}O_{3}$.AIN) 및 $\Phi$($5Al_{2}O_{3}$.AIN)상 등의 2차상을 생성하는 것에 기인된다. 20 및 25 mol% AIN이 첨가된 알루미나 소결체의 열전도도는 $1800^{\circ}C$에서 최대값을 나타내며, $1600^{\circ}C$에서는 $\alpha$-$Al_{2}O_{3}$ 및 ALON상이 존재하나 그 이상의 온도에서는 모두 ALON상만이 존재하였다.