Abstract
Shrinkage behaviors associated with forming drying and firing processes could be a driving force for the densification in materials. Low shrinkage-densification behaviors in clay materials have been shown to be highly dependent upon the processing parameters including particle size effect and kinetic behaviors caused by phases transformation characteristics. Chamottes pre-treated at 90$0^{\circ}C$ and 120$0^{\circ}C$ had dominent influence upon shrinkage control of materials during heat-treatment. But Coarse chamotte particles heat-treated at 120$0^{\circ}C$ did not contri-bute to any densification behaviors in clay materials while these added coarse particles could enhance near-net-shape control. Microstructure / property relationships in clay materials have been thought to be directly influenced by optimized characteristics between low shrinkage and densification behaviors.
점토질 소지에 있어서 수축 특성은 성형, 건조 및 소성 공정에 수반되어 치말화거등에 기여할 수 있는 구동력이 될 수 있다. 점토질 소지에서 저수축 치말화거동은 입자크기효과와 상전이 특성에 기인하는 열간 반응전이 거동을 포함하는 공정변수에 따라 크게 변화됨을 보였다. 90$0^{\circ}C$ 및 120$0^{\circ}C$에서 열처리된 Chamotte의 첨가를 통해서 점토질 소지의 열간 치밀화 과정에 기인하는 공정수축은 크게 억제될 수 있었다. 120$0^{\circ}C$에서 열처리된 조대한 Chamotte 입자는 점토 소지의 치밀화 거동을 억제하여 치밀한 소결미세구조를 얻을 수는 없었지만, 조대한 Chamotte 입자의 첨가는 neat-net-shape 제어를 촉진할 수 있었다. 점토질 소지에 있어서 미세구조/물성간의 연관관계는 저수축과 치밀화 거동사이의 상반된 특성을 제어함으로써 얻어진 최적조건에 따라 직접적인 영향을 받을 것으로 판단되었다.