Abstract
Quantitative analysis each portland cement components was conducted by standard calibration method using X-ray fluorescence spectrometer. Standard sample and the unknown sample were prepared by fused cast bead method. In checking the errors of standard cement 227A372 the relative errors of constituents such as CaO, SiO2, Al2O3, Fe2O3, MgO and SrO were less than 1% and the relative errors of constituents such as So3, K2O, TiO2, Na2O P2O5, and Mn2O3 were less than 5% Sample preparation was mainly contributed to the errors. Compared with general wet chemical method the results of X-ray fluorescence analyses were more precise and accurate. Moreover it is possible to analyze precisely a little amount of the constituents such as SrO, Mn2O3 and P2O5 the analyses of which were very difficult using the wet chemical method.
X-선 형광분석법을 사용하여 표준검정곡선법으로 시멘트 중의 주, 부성분들을 정량하고 습식법과 분석결과를 비교하였다. 이때, 표준시료 및 미지시료는 용융 케스트 비드법으로 준비하였다. 표준시멘트(227A372)의 오차분석결과 주성분인 CaO, SiO2, Al2O3, Fe2O3 및 부성분중의 MgO, SrO는 상대오차가 1% 이내이었으며, 부성분중 So3, K2O, TiO2, Na2O P2O5 및 Mn2O3는 5% 이하의 상대오차를 가졌다. 부성분의 상대오차는 시료준비오차가 가장 큰 부분을 차지하였다. X-선 형광분석과 습식분석을 비교한 결과 시멘트 분석의 측정값간의 최대혀용범위를 만족하므로, X-선 형광분석법을 시멘트 화학분석에 적용할 수 있을 것으로 판단된다. 그리고, 기존의 습식법으로 분석하기 어려운 시멘트내에 존재하는 미량성분인 P2O5, SrO 및 Mn2O3 의 정밀정확한 분석 또한 가능하였다.