Abstract
M type hexa-ferrites were prepared by means of a solid state reaction using mill scale, $Fe_{2}O_{3}$, and the mixture of mill scale and $Fe_{2}O_{3}$. The mixture of powders were calcined at $1150^{\circ}C$ for 2 hrs. and sintered at $1250^{\circ}C$ for 2 hrs, with varing the mole ratio of $Fe_{2}O_{3}$/$BaCO_{3}$, by 5.2~6.0. And the magnetic properties and morphologies of Baferrites with impurities such as $SiO_{2},\;Al_{2}O_{3},\;MgO,\;CaO\;and\;Na_{2}O$ in the mill scale were investigated. The magnetic properties were worsened by the addition of $Na_{2}O because of non-reacted iron oxide and intermediate compound of $BaFe_{2}O_{4}$ but they were improved apparently by the addition of $Si_{2}$ and $Al_{2}O_{3}$ in the composition of $BaO.5.6Fe_{2}O_{3}$. Moreover, $M_{s}$ decreased but $_{B}H_{C}$ increased through the addition of $Al_{2}O_{3}$ in Ba-ferrite. ${(BH)}_{max}$ of sintered BM($BaCO_{3}$, mill scale mixture) and BFM($BaCO_{3}$, $Fe_{2}O_{3}$, and null scale mixture) were 0.86 and 1.04 MGOe, respectively, and the magnetic properties were changed around $440^{\circ}C$.
제철소의 부산물인 mill scale과 $Fe_{2}O_{3}$, 그리고 이들의 혼합물을 사용하여 M형 ferrite를 제조하였다. $Fe_{2}O_{3}$와 $BaCO_{3}$의 몰비를 5.2~6.0으로 변화시킨 혼합물의 하소 및 소결은 각각 $1150^{\circ}C,\;1250^{\circ}C$에서 2시간 행하였으며, 하소시에 mill scale 중의 불순물 성분인 $SiO_{2},\;Al_{2}O_{3},\;MgO,\;CaO\;및\;Na_{2}O$를 적당량 첨가한 시편으로 자기적 특성과 형상을 조사하였다. $Na_{2}O$를 첨가한 시편은 미반응의 $Fe_{2}O_{3}$와 중간 화합물인 $BaFe_{2}O_{4}$의 영향으로 자기적 특성이 감소하였으나, $BaO.5.6Fe_{2}O_{3}$ 조성에 $SiO_{2}$와 $Al_{2}O_{3}$의 첨가는 특성의 증진을 보였으며, 특히 $Al_{2}O_{3}$는 $M_{s}$ 값은 감소시켰으나 $_{B}H_{c}$ 값을 증가시켰다. BM($BaCo_{3}$와 mill scale의 혼합물)과 BFM($BaCO_{3},\;Fe_{2}O_{3}$, mill scale의 혼합물) 소결 시편의 ${(BH)}_{max}$는 각각 0.86, 1.04 MGOe였으며, $440^{\circ}C$ 부근에서 자기 특성의 변화를 보였다.