Needle-like $\alpha-Fe_{2}O_{3}$ particles as precursor for magnetic recording media were prepared directly from amorphous ferric hydroxide in the aqueous solution by hydrothermal reaction. Ellipsoidal or rectangular $\alpha-Fe_{2}O_{3}$ particles were formed in the range of pH 10.75~11.75. The length and acicularity of $\alpha-Fe_{2}O_{3}$ particles were decreased gradually with increasing of citric acid concentration. The formation of needle-like $\alpha-Fe_{2}O_{3}$ particles was inhibited above citric acid concentration of $1.5{\times}10^{-4}\;mol$. We can synthesize $\alpha-Fe_{2}O_{3}$ particles with the most superior acicularity at $140^{\circ}C$ and can not expect a good needle-like particles above $220^{\circ}C$.
자기 기록용 전구체에 적합한 침상형 $\alpha-Fe_{2}O_{3}$ 입자를 수열반응법에 의해 수용액 중에서 비정질 수산화제이철로부터 직접 제조하였다. Ellipsoidal 또는 rectangular 형상의 $\alpha-Fe_{2}O_{3}$ 입자는 염기도 10.75~11.75 범위에서 생성되었다. 구연산 농도가 증가함에 따라 침상 입자의 길이와 침상비는 점차 감소하였으며, 구연산 농도 $1.5{\times}10^{-4}\;mol$ 이상 일때는 침상형 $\alpha-Fe_{2}O_{3}$ 입자로의 결정화가 저해되었다. 수열 반응 온도 $140^{\circ}C$에서 가장 침상성이 우수한 $\alpha-Fe_{2}O_{3}$ 입자가 제조되었으며, $220^{\circ}C$ 이상에서는 침상형 입자의 생성을 기대할 수 없었다.