A Study on Difference in Coercivity between Substituted Barium Ferrite Powder and Its Tape

자기기록용 치환형 Ba-Ferrite 분말과 Tape의 보자력 차이에 관한 연구

A coercivity of barium ferrite (BaM) tape was found to be higher than the coercivity of BaM powder, This difference is in the range of 50 Oe to 600 Oe, which depends on substituted cations. physical properties of powder, and preparation conditions of the tape. The coercivity difference is attributed to both particle stacking and adsorption of organic solvent on particle surface. Regardless of substituted cations, the coercivity of longitudinally oriented BaFe tape was higher than that of BaM powder by a range of 100 Oe to 120 Oe, which is caused by particle stacking' During the active adsorption process on preparation of magnetic paint, where MEK (methyl ethyl ketone), TOL (toluene) and CHO (cyclohexanone) were used, chemisorption of solvents on the surface of substituted BaFe particle occurred to form polymeric compounds surrounding the particle. An increase in coercivity, caused by the solvent adsorption, was significant for Co-substutited BaM tape. Among these solvents CHO was the most effective one in increasing the coercivity of the Co-Ti substituted BaM tape.

기존의 침상형 매체와는 다르게 자기기록용 치환형 Ba-ferrite(BaM) tape의 보자력은 입자특성, 치환이온의 종류 및 tape 제조조건에 따라 분말의 보자력보다 50 Oe에서 600 Oe로 높게 나타났다. 이 보자력 증가는 육각판상 입자간 stacking 효과와 분말표면에 유기용제 흡착효과에 기인하였다. 동일한 입자크기와 판상비를 갖지만 치환이온이 다른 BaM 분말을 사용한 수평배향된 tape의 경우 입자간 stacking 효과에 의한 보자력 증가는 100 Oe에서 120 Oe 사이로 일정하여 치환이온의 종류에 무관하였다. 치환형 BaM 분말표면에 유기용제 흡착은 활성화 흡착과정에 의해 이루어졌으며, 유기용제 흡착에 의한 보자력 증가는 Co 이온이 함유된 BaM tape에서만 나타났다. Co-Ti 치환된 BaM의 경우 tape 제조시 사용된 유기용제 MEK(methyl ethyl ketone), TOL(toluene) 및 CHO (cyclohexanone) 중에서 CHO가 보자력 증가에 가장 크게 기여하였다.