Preparation of High Range Water Reducers Containing Carboxylic Acid and Their Cement Dispersion Properties(III)

카르본산계 고성능감수제의 제조 및 그들의 시멘트 분산특성(III)

  • 김원기 (동양중앙연구소) ;
  • 황재현 (동양중앙연구소 건설재료연구실) ;
  • 김우성 (경북대 고분자공학과 대학원생) ;
  • 김영진 (경북대 고분자공학과 대학원생) ;
  • 강인규 (경북대 고분자공학과)
  • Published : 1996.08.01
Download PDF
⟨ Previous Next ⟩

Abstract

Styrene-maleic anhydride copolymers with different composition (1:1SMA. 5:1SMA) were synthesized and further reacted with sulfuric acid to obtain water soluble copolymers (1:1SSMA, 5:1SSM.4). In the flow experiments of cement mortar mixed with copolymers, 5:1SSMA showed higher fluidity than 1:1SSMA. The cement mortar mixed with 1% 5:1SSMA maintained 95% of original flow after 60 min. On the other hand, the compressive strength of the hardened cement mortars containing 0.5% copolymers after 28 days curing was also examined. The compressive strength of hardened cement mortar containing 5:1SSMA was increased up to 41% compared to the plain while 1:1SSMA was increased up to 29%. As the results, the 5:1SSMA used in this study are greatly expected as a new high range water reducers for the concrete.

화학조성이 다른 스티렌-무수말레인산 공중합체(1:1SMA, 5:1SMA)를 합성하고 이들을 황산화하여 수용성의 공중합체(1:1SSMA, 5:1SSMA)를 제조하였다. 이들 공중합체를 첨가한 시멘트 모르타르의 유동특성을 조사한 결과, 5:1SSMA는 1:1SSMA보다 우수한 플로우를 나타내었다. 또한 5:1SSMA를 1%첨가한 시멘트 모르타르는 60분 후에도 95% 이상의 플로우를 유지하였다. 한편 합성고분자를 0.5% 첨가한 경화시멘트 모르타르의 압축강도도 조사하였다. 그 결과 5:1SSMA를 첨가한 시험체의 28일 압축강도는 첨가하지 않은 시험체보다 41%증가한 반면 1:1SSMA는 29%의 증가를 나타내었다. 본 연구에서 제조한 5:1SSMA는 새로운 카르본산계 고성능감수제로서 그 활용이 크게 기대되어 진다.