The Physical and Mechanical Properties of No-Fines Lightweight Concrete Using Synthetic Lightweight Coarse Aggregate

인공경량조골재(人工輕量粗骨材)를 사용(使用)한 무세골재(無細骨材) 경량(輕量)콘크리트의 물리(物理)·가학적(加學的) 특성(特性)

  • Kim, Seong Wan (Dept. of Agricultural Engineering, Coll. of Agriculture, Chungnam National Univ.) ;
  • Min, Jeong Ki (Dept. of Agricultural Engineering, Coll. of Agriculture, Chungnam National Univ.) ;
  • Cho, Seung Seup (Dept. of Agricultural Engineering, Coll. of Agriculture, Chungnam National Univ.) ;
  • Sung, Chan Yong (Dept. of Agricultural Engineering, Coll. of Agriculture, Chungnam National Univ.)
  • 김성완 (충남대학교 농과대학 농공학과) ;
  • 민정기 (충남대학교 농과대학 농공학과) ;
  • 조성섭 (충남대학교 농과대학 농공학과) ;
  • 성찬용 (충남대학교 농과대학 농공학과)
  • Published : 1996.06.30

Abstract

The normal cement concrete is widely used material to build the construction recently, but it has a fault to increase the dead load on account of its unit weight is large compared with strength. So, many engineers are continuously searching for new materials of construction to provide greater performance at lower density. Many studies were carried out on the lightweight aggregate concrete in foreign country in the latter half of the 19th century, therefore lightweight aggregate concrete has been used successfully for many years for structural members. The main purpose of the work described in this paper were to establish its physical and mechanical properties of no-fines lightweight concrete using synthetic lightweight coarse aggregates. Test results are summarized as follows ; The water-cement ratio was shown less than 33% in use synthetic lightweight coarse aggregates, unit weights of synthetic lightweight concrete was shown less than $1,800kg/m^3$ and compressive strength was higher than $200kg/m^2$. And the pulse velocity was more than 3,000m/sec. The relationship of compressive strength between unit weight and pulse velocity was shown to be approximately linear.

본 연구는 세골재를 사용하지 않고 인공경량조골재로써 팽창점토와 경석을 사용한 인공경량골재 콘크리트의 물리 역학적 특성을 구명하기 위하여 실시되었으며, 시험을 통하여 얻어진 결과를 요약하면 다음과 같다. 1. 물-시멘트비는 팽창점토를 사용한 경우 31%, 경석을 사용한 경우는 33%로 나타남으로써, 인공경량골재에 따른 물-시멘트비의 차이는 크게 나타나지 않았다. 2. 단위중량은 팽창점토를 사용한 경우 $1,635kg/m^3$, 경석을 사용한 경우는 $1,790kg/m^3$로, 경석을 사용함으로써 다소 증가하는 것으로 나타났다. 3. 흡수율은 모든 사용골재에서 다 같이 10%이하로 작게 나타났으며, 팽창점토보다 경석을 사용함에 따라 약간 증가하는 경향을 보였다. 4. 압축강도는 팽창점토와 경석을 사용한 경우 $203kg/m^2$$237kg/m^2$로 거의 유사하게 나타났으며, 인장강도와 휨강도도 압축강도와 마찬가지로 사용골재에 따른 차이는 크게 나타나지 않았다. 5. 반발도는 압축강도가 클 수록 크게 나타났고, 압축강도와 고도의 유의성이 있었으며, 특히 저강도 영역에서의 상관성이 크게 나타났다. 6. 초음파진동속도는 팽창점토와 경석을 사용한 경우 $3,884kg/m^2$, $3,922kg/m^2$로써 사용골재에 따른 차이는 거의 없는 것으로 나타났으며, 단위중량 및 압축강도가 클 수록 증가하는 경향을 보였다.