Abstract
The NR films were prepared with mixing of natural rubber latex(NRL) with various additives, and NR/CR films were prepared by blend ratio of chloroprene rubber latex(CRL). The swelling degree and the mechanical properties of these films were measured according to the procure time. As a result, optimum condition were showed the swelling degree : 80~85%, precure time : 48~60hrs., and tensile strength was reduced but elongation was increased as increasing the blend ratio of CRL. On the mechanical properties of films prepared by different dipping process in these optimum condition, the tensile strength and tear strength of NR/CR films by one dipping process are better than NR-d-CR films by two dipping process. The surface of these films were observed with scanning electron microscopy(SEM). It was found that phase separation was occured as increasing the blend ratio of CRL.
천연고무 라텍스(NRL)와 각종 첨가제를 배합 숙성하여 NR 필름을 제조하였고, 클로로프렌고무 라텍스 (CRL)를 일정한 비율로 블렌드하여 NR/CR 필름을 제조하였다. 이들 필름의 전가류 시간에 따른 팽윤도와 기계적 성질의 변화를 측정한 결과, 팽윤도 80~85%, 전가류 시간 48~60hrs등에서 가장 우수하였고, CRL의 블렌드 비율이 증가함에 따라 인장강도는 감소하고 신장율은 증가하는 경향을 나타내었다. 제조공정을 달리하여 제조한 시편의 기계적특성을 비교한 결과, 1회 디핑법을 사용한 NR/CR 필름의 인장강도, 인열강도는 2회 디핑한 NR-d-CR 필름보다 더 우수하였다. 이들 시편의 표면을 SEM으로 관찰한 결과, CRL의 블렌드 비율이 증가할수록 필름 표면의 벌크한 집합체가 증가되는 것으로 보아 상분리가 일어났음을 관찰할 수 있었다.