Abstract
The composite $MgF_2$-$TiO_2$ films are fabricated by codeposition from two independent sources. To improve optical and mechanical properties of films, the films are prepared by ion-assisted deposition. Chemical compositions, optical properties and microstructures of the composite films were investigated. The chemical composition rates of Ti:Mg of $MgF_2$-$TiO_2$ composite films are nonlinearly varied according to the relative deposition rate. It is found that the refractive indices of the composite films decrease with increasing $MgF_2$ contents and can be fitted quite well with Drude's formula and that the microstructures of the composite films changes from an amorphous to crystalline with increasing $MgF_2$ mole fractions.
MgF$_{2}$와 TiO$_{2}$를 각각 다른 두 증발원으로부터 동시에 증착시켜 혼합 박막을 제작하였다. 박막의 특성을 개선시키기 위해 이온 보조 증착(IAD)을 하였다. 제작된 MgF$_{2}$-TiO$_{2}$ 혼합 박막의 원소 조성비, 광학적 특성과 결정 구조를 분석하였다. 상대적 증착률을 달리하여 제작된 MgF$_{2}$-TiO$_{2}$ 혼합 박막의 Mg:Ti의 조성비는 비선형적으로 변화하였으며, MgF$_{2}$의 조성비를 상대적으로 증가시킴에 따라 혼합 박막의 굴절률은 감소하였고 Drude 모델을 잘 만족함을 알 수 있었다. 그리고 MgF$_{2}$의 조성비가 증가할수록 비정질인 TiO$_{2}$ 구조 사이에 다결정질인 MgF$_{2}$의 양이 증가하여 결정성을 갖는 박막으로 성장함을 확인하였다.