Abstract
Water-soluble phosphate glasses containing Ag and Cu ion were prepared through melting process. Dis-solution characteristics, bactericidal effect and cytotoxicity were investigated with composition and time in D. I. water using the powdered sample. Surface change were observed with increasing dissolution time us-ing the bulk specimen. Dissolution amount was maximum at the molar Ag:Cu ratio of 1 and increased with increasing time. The behavior of dissolution was total dissolution from the early stage. But no new layer was observed at the glass surface during dissolution. The bactericidal effect for pseudomonas sp, e. coli, sta-phylococcus aureus, and salmonella increased with increasing dissolution amount and therefore great bac-tericidal effect appeared. The result of cytotoxicity experiment to L929 showed that solution with more than 10 ppm of Ag ion had strong cytotoxicity.
은 이온과 구리 이온을 동시에 함유하는 살균용 인산염계 수용성 유리를 용융법으로 제조하였다. 분말상의 유리 시편을 상온의 증류수에 넣어 조성과 시간에 따른 용해 특성을, bulk상 시편에 대해서는 용해 전.후의 표면변화를 각각 관찰하였고, 살균 효과 및 세포독성을 평가하였다. 은 이온:구리 이온=1:1인 조성에서 최대 용해량을 나타내었으며 용해거동은 초기부터 total dissolution이 지배적이었다. 시간의 경과에 따라 용해는 진행이 되지만, 표면에 생성되는 새로운 층은 관찰되지 않았다. Pseudomonas sp, e. coli, staphylococcus aureus, 및 salmonella균에 대한 살균 효과는 용해량의 증가에 따라 증가하여 우수한 살균효과를 나타내었다. L929 세포에 대한 독성 실험 결과, 은 이온의 농도가 10ppm이상에서만 독성을 나타내었다.