High-Temperature Degradation of Hot-Pressed $t-ZrO_2$ Co-doped with $Y_2O_3$ and $Nb_2O_5$

Hot-press법으로 제조된 $Y_2O_3$와 $Nb_2O_5$가 첨가된 정방정 ZrO2의 고온열화

  • Published : 1997.09.01
Download PDF
⟨ Previous Next ⟩

Abstract

Tetragonal ZrO2 polycrystal (TZP), consisted of 90.24 mol% ZrO2-5.31 mol% Y2O3-4.45 mol% Nb2O5, were prepared using hot-press and mechanical properties and high-temperature degradation were investigated. The specimen, hot-pressed for 1 h at 140$0^{\circ}C$ in Ar atmosphere, exhibited flexural strength of 1010 MPa and fracture toughness of 7.5 MPam1/2 and experienced no low-temperature degradation below 40$0^{\circ}C$. However, as aged for 100h at temperatures higher than 40$0^{\circ}C$, TZP was suffered by high-temperature degradation due to an extensive cavitation caused by the oxidation of carbon. XPS observation revealed that the carbon incorporated in TZPs during hot-pressing exists as either an ether-type CO or a carbonyl-type C=O. Despite of the high-temperature degradation of t-ZrO2 co-doped with Y2O3 and Nb2O5, its flexural strength and fracture toughness were superior to those of the commercial 3 mol% Y2O3-TZP hot-pressed under the identical condition as determined before and after the aging treatments.

Keywords

References

  1. J. Mater. Sci. v.23 Sintering of 3mol%Y₂O₃-TZP and its fracture after ageing treatment S. Chen;H. Lu
  2. J. Am. Ceram. Soc. v.70 no.8 Low-temperature aging of t-ZrO₂polycrystals with 3 mol%Y₂O₃ H. Lu;S. Chen
  3. J. Mater. Sci v.30 The effect of ceria co-doping on chemical stability and fracture toughness of Y-TZP M. M. R. Boutz;A. J. A. Winnubst;B. Van Langerak;R. J. M. Olde Scholtehuis;K. Kreuwel;A. J. Burggraaf
  4. Ceramic Transactions(Ceramic Powder Science Ⅲ) no.12 Effects of oxide additions on the stability of the tetragonal phase in TZP ceramics H. Hofmann;B. Michel;L. J. Gauckler;J. Allemann;G. L. Messing(ed.);S. Hirano(ed.);H. Hausner(ed.)
  5. 한국요업학회지 v.34 no.6 Y₂O₃와Nb$_2O_5$가 첨가된 ZrO₂의 상 안정성 및 물리적 성질 이득용;김대준;조경식;장주웅
  6. Solid State Ionics v.80 Phase transformation of Y₂O₃and Nb₂O5 doped with tetragonal zirconia during low temperature aginig in air D.-J.Kim;H. -J.Jung;D. -H. Cho
  7. J. Euro. Ceram. Soc. v.17 no.7 Influence of aging environment on low temperature degradation of tetragonal zirconia alloys D.-J. Kim
  8. J. Am. Ceram. Soc. v.77 no.5 Effect of dopants on zirconia stabilization-an X-ray absorption study;Ⅲ,charge-compensating dopants P. Li;I. Chen;J. E. Penner-Hahn
  9. J. Am. Ceram. Soc. v.69 no.8 Mechanical properties of Y₂O₃-stabilized tetragonal ZrO₂polycrystals after ageing at high temperature T. Masaki
  10. J. Am. Ceram. Soc. v.69 no.8 Average grain size in polycrystalline ceramics M. J. Mendelson
  11. J. Am. Ceram. Soc. v.55 no.6 Phase analysis in zirconia system R. C. Garvie;P. S. Nicholson
  12. J. Am. Ceram. Soc. v.59 Fracture toughness determinations by indentation A. G. Evans;E. A. Charles
  13. Comm. Am. Ceram. Soc. v.66 no.11 A modifield indentation toughness technique R. F. Cook;B. R. Lawn
  14. J. Vac. Sci. Technol A v.14 no.2 Chemical shifts and optical properties of tin oxide films grown by a reactive ion assisted deposition W. Choi;H. Jung;S. Koh
  15. CRC Handbook of Chemistry and Physics(61st Ed.) R. C. Weast(ed.);M. J. Astle(ed.)
  16. J. Am. Ceram. Soc. v.79 no.9 Effect of refractory oxides on the oxidation of graphite and amorphous carbon A. Yamaguchi;S. Zhang;J. Yu