Growth and characterization of a Bi-Sr-Ca-Cu-O phase by crystal pulling method

Crystal pulling법에 의한 Bi-Sr-Ca-Cu-O계의 결정 성장과 특성 평가

  • Yoon, D.H. (Department of Materials Science and Technology, Iwate University) ;
  • Sato, N. (Department of Materials Science and Technology, Iwate University) ;
  • Yoshimoto, N. (Department of Materials Science and Technology, Iwate University) ;
  • Yoshizawa, M. (Department of Materials Science and Technology, Iwate University)
  • 윤대호 (암수대학 공학부 재료물성공학과) ;
  • 좌등혜유 (암수대학 공학부 재료물성공학과) ;
  • 길본칙지 (암수대학 공학부 재료물성공학과) ;
  • 길택정인 (암수대학 공학부 재료물성공학과)
  • Published : 1997.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

The $Bi_2Sr_2Ca_{n-1}Cu_nOy$(BSCCO) phase is well known to be a superconductor having a strong anisotropic behavior. It can be seen that it is difficult to control the growth direction. In this study, we try to grow a Bi-Sr-Ca-Cu-O phase crystal by the crystal pulling method with a seed crystal and crucibel rotation. Relatively large crystals of the order of $5{\times}5{\times}5{\textrm}{mm}^3$ dimensions can be obtained. We also discuss the possible crystallization field of the $BiO_{1.5}$-(Sr, Ca)O-CuO ternary phase diagram, and present some results of the characterization and magnetic measurements on the grown crystal.

$Bi_2Sr_2Ca_{n-1}Cu_nOy$(BSCCO)계는 강한 이방성의 움직임을 갖는 초전도체로서 잘 알려져 있으며, 결정육성시 성장방향의 제어에 큰 어려움이 있다. 본 연구에서는 종자 결정과 도가니의 회전을 이용한 crystal pulling법을 이용하여 Bi-Sr-Ca-Cu-O계의 결정성장을 시도하였으며, 이로부터 $5{\times}5{\times}5{\textrm}{mm}^3$ 크기의 비교적 큰 결정을 성장하였. 또한 성장결정의 초전도 특성을 조사하였으며, $BiO_{1.5}$ -(Sr, Ca)O-CuO 3원 상태도에서의 결정화 가능 영역을 검토하였다.