On the study of $AlSiCa(Al_2O_3-SiC-C)$ refractories: (II) Oxidation and sintering of the synthesized powders

$AlSiCa(Al_2O_3-SiC-C)$계 내화물 재료에 관한 연구:(II) 합성원료의 산화 및 소결 특성

It was succeeded in synthesizing the $Al_2O_3$-SiC refractory powders, which is main raw material of AlSiCa, from the domestic Hadong Kaolin. The oxidation reaction of the synthesized $Al_2O_3$-SiC powder was examined. The activation energy for SiC in $Al_2O_3$-SiC powder was calculated to be $\Delta$G=74.86 KJ/mol in air, however the poor sinterability of the powders is thought to be due to the vaporization of SiC in $H_2$ atmosphere. The formation of the whisker-SiC gives the possibility in use for high temperature structural material over high temperature refractory brick.

국산 하동고령토로부터 AlSiCa의 주원료인 $Al_2O_3$-SiC계 내화물 원료를 합성하는 데는 성공하였으며, 합성된 $Al_2O_3$-Sic 합성분말의 산화반응을 검토하였다. 공기중에서 산소와 반응시켜 Sic가 $SiO_2$로 산화될 때 필요한 활성화 에너지는 $\Delta$G=74.86 KJ/mol 이었으며, 수소분위기에서 $1500^{\circ}C$ 및 $1600^{\circ}C$에서 상압소성한 결과 vaporization 현상때문에 소결특성이 좋지 않았다. whisker-SiC상태로 합성되는 이 복합체는 AlSiCa의 고온내화벽돌이외의 고온구조용 재료로 응용될 수도 있다.