Preparation of $Pb(Sc_{1/2}Nb_{1/2})O_3$ Powders by the molten salt synthesis method

솔-젤법에 의한 $Pb(Sc_{1/2}Nb_{1/2})O_3$ 분말의 제조

  • ;
  • ;
  • D. A. Payne
  • 박경봉 (안동대학교 재료 공학과) ;
  • 김태희 (안동대학교 재료 공학과) ;
  • Published : 1997.11.01
Download PDF
⟨ Previous Next ⟩

Abstract

Lead scandium niobate $Pb(Sc_{1/2}Nb_{1/2})O_3$ powders were prepared by the sol-gel method using lead acetate, scandium acetate, and niobium isopropoxide as precursors. Crystallization behavior and phase formation were investigated for gel-derived powders. After the calcination at $700^{\circ}C$ for 1 hr, $Pb(Sc_{1/2}Nb_{1/2})O_3$ powder with the purity of 97% was formed and the average particle size of powder was below 0.2 $\mu \textrm{m}$.

lead acetate, scandium acetate, niobium isopropoxide를 전구체로 사용한 솔-젤법으로 $Pb(Sc_{1/2}Nb_{1/2})O_3$ 분말을 제조하였다. 젤 분말에 대한 결정화 거동과 상변화가 연구되었다. 솔-젤법을 이용하여 $700^{\circ}C$에서 1시간 동안 열처리를 행하여 97 % 이상의 매우 순수한 $Pb(Sc_{1/2}Nb_{1/2})O_3$ 상을 얻을 수 있었으며 0.2 $\mu \textrm{m}$ 이하의 평균 입자 크기를 가진 매우 미세한 분말의 제조가 가능하다.