Physical and Mechanical Properties of Surlightweight Polymer Concrete

초경량(超輕量) 폴리머 콘크리트의 물리(物理)·역학적(力學的) 특성(特性)

This study was performed to evaluate the physical and mechanical properties of surlightweight polymer concrete using synthetic lightweight aggregate. The following conclusions were drawn; 1. Unit weight was in the range of $810~970kgf/m^3$, the unit weights of those concrete were decreased 58~65% than that of the normal cement concrete. 2. The highest strength was achieved by $P_1$, it was increased 112% by compressive strength, 378% by bending strength and 290% by tensile strength than that of the normal cement concrete, respectively. 3. Ultrasonic pulse velocity was in the range of 2,206~2,595m/s, which was low showed compared to that of the normal cement concrete. 4. Durability of surlightweight polymer concrete was superior to that of the normal cement concrete. 5. Compressive, tensile and bending strength were largely showed with the increase of unit weight. But, ultrasonic pulse velocity was low showed with the increase of unit weight.

이 연구는 폴리머와 인공경량 세골재 및 인공 경량 조골재를 사용한 초경량 폴리머 콘크리트의 물리 역학적 특성을 구명한 것으로서, 이 연구를 통해 얻어진 결과를 요약하면 다음과 같다. 1. 단위중량은 배합비의 종류에 따라 $810{\sim}970kgf/m^3$로서, 보통 시멘트 콘크리트에 비해 58~65%정도 감소되었다. 2. 강도는 $P_1$에서 가장 크게 나타났으며, 보통 시멘트 콘크리트에 비하여 압축강도는 112%, 휨강도는 378%, 인장강도는 290%가 각각 증가되었다. 3. 초음파진통속도는 2,206~2,595m/s 정도로 보통 시멘트 콘크리트보다 약간 작게 나타났으며, 인공경량 세골재의 양이 적을수록 크게 나타났다. 4. 내구성은 보통 시멘트 콘크리트에 비하여 뛰어난 효과를 보였으며, 특히 산을 접하는 구조물에 사용하면 효과가 매우 클 것으로 기대된다. 5. 압축강도, 인장강도 및 휨강도는 단위중량이 감소할수록 작게 나타났으며, 초음파진동속도는 단위중량이 감소할수록 크게 나타났다.