Abstract
The etching experiments for n-GaN were done using the wet chemical, photo-enhanced-chemical and electro-chemical etching methods. The experimental results show that n-GaN is etched is diluted NaOH solution at room temperature and the removed thickness of n-GaN is linearly increased with etching times. The etching rate of the photo-enhanced-chemical and electro-chemical etching methods are several times higher than that of the wet chemical method. The maximum etching rate of n-GaN with $n{\fallingdotseq}1{\times}10^{19}cm^{-3}$ was 164 $\AA$/min under the experimental condition of the Photo-enhanced-chemical etching. The etching rates of n-GaN are very much dependant on the electron concentrations of the samples. The pattern is $100{\mu}m{\times}100{\mu}m$ rectangulars covered with $SiO_2$film. It is shown that the etched side-wall charactistics of the pattern is vertical without dependance of the n-GaN orientations, and the smoothness of etched n-GaN surface is fairly flat.
GaN계 재료의 습식 화학식각 특성과 광 화학 및 전기 화학 및 전기 화학 습식식각 특성을 연구하였다. n형 GaN는 상온에서 NaOH 수용액에 식각되었으며 식각두께는 식각시간에 선형적으로 증가하였다. 또 광 조사 및 전기 화학을 가할 경우 식각율은 수배로 증가하였으며, 식각율은 $1{\times}10^{19};cm^{-3}$의 전자농도를 갖는 시료에서 광 조사시 최대 164${\AA}$/min을 얻었다. n-GaN의 식각율은 GaN의 전자농도에 크게 의존하는 특성을 나타내었으며 이러한 식각과정을 논의하였다. $SiO_2$ 박막으로 덮여진 100${\mu}m{\times}100{\mu}m$ 모양의 옆 식각면은 방향성을 갖지 않고 수직하였으며, 넓은 면적에서 매우 평탄하였다.