Abstract
The synthesis of $Sr_{1-x}Eu_xAl_2O_4$ (x=0.005~0.2;mol%) phosphors and its properties of both photoluminescence and long-phosphorescent were investigated as a function of $Eu_2O_3$ composition. The peak wavelengths (520 nm) of phosphorescence spectra were found not to vary with the $Eu_2O_3$ composition (x) of $Sr_{1-x}Eu_xAl_2O_4$ crystals. Single phase of $SrAl_2O_4$ which determined by XRD and PL was obtained with the compositions of x<0.05 mol%. After the removal of light excitation (360 nm), the excellent after-glow characteristics of the phosphorescence were obtained with the $Eu_2O_3$ compositions of x<0.05 mol%, although the after-glow intensities for all phosphors vary exponentially with the times.
부활제인 $Eu_2O_3$의 농도를 변화시킨 $Sr_{1-x}Eu_xAl_2O_4$(x=0.005~0.2mol%)계 장잔광 형광체를 98%Ar+2% H2의 환원분위기에서 고상반응시켜 합성한 후 X-선 회절실험과 장잔광 축광재료로서 가장 중요한 발광특성과 장잔광 특성을 조사하였다. $SrAl_2O_4:Eu^{2+}$계 형광체는 $Eu_2O_3$의 농도에 관계없이 녹황색의 520nm파장을 최대 발광파장으로 하는 발광스펙트럼을 나타내었으나, 발광특성을 크게 저해하지 않는 SrAl2O4의 단일상을 얻기 위한 농도는 0.05mol% 이하가 적절하였다. 또한 $SrAl_2O_4:Eu^{2+}$ 형광체의 잔광강도는 $Eu_2O_3$의 농도에 무관하게 시간에 따라 모든 시료에서 지수 함수적으로 감소하나, Eu2O3의 농도가 0.05mol% 이하인 경우에 발광의 감쇠속도가 작은 뛰어난 장잔광특성을 나타내었다.