Abstract
Sintering behavior and dielectric peroperties of $xCaTiO_3-La(Zn_{1/2}Ti_{1/2})O_3$ system were investigated for better understanding of the microwave dielectric materials. In $xCaTiO_3-(1-x)La(Zn_{1/2}Ti_{1/2})O_3$ systems, solid solution type was focused as a function of composition(x=0.4-0.6) and sintered density. With increasing the sintered density, the relative dielectric constant was decreased and Q value was increased and then saturated. In solid solution type, dielectric constant was increased with increasing $CaTiO_3$ content. In $0.5\;CaTiO_3-0.5\; La(Zn_{1/2}Ti_{1/2})O_3$ case, dielectric constant(=48) and temperature coefficient of resonace frequency$(=-1 ppm/^{\circ}C$) were obtained.
마이크로파 유전체로 응용되는 $xCaTiO_3-La(Zn_{1/2}Ti_{1/2})O_3$계의 소결시 고용조성 변화(x=0.4-0.6) 및 소결거동에 따른 유전특성에 조사하였다. 소결밀도가 감소함에 따라 유전상수는 감소하였으며 품질계수(Q)는 증가하다 일정한 값을 유지하였다. 고용체형의 경우 유전상수는 $CaTiO_3$조성 증가에 따라 증가하였다. $0.5\;CaTIO_3\;0.5\;La(Zn_{1/2}Ti_{1/2})O_3$의 경우 유전상수 48, 온도계수는 $-1ppm/^{\circ}C$를 나타내었다.