Characterizations of lithium niobate single crystals grown from melt with $K_2O$

$K_2O$를 첨가한 융액으로부터 성장시킨 Lithium Niobate 단결정의 특성

  • Published : 1998.08.01

Abstract

A series of $LiNbO_3$ single crystals were grown by the Czochralski method from a congruent melt, a congruent melt with 0.05 mol% $Fe_2O_3$, a congruent melt with 6 wt.% $K_2O$ and a congruent melt with 6 wt.% $K_2O$ and 0.05 mol% $Fe_2O_3$ respectively. The growth of $LiNbO_3$ crystal from a congruent melt 6 wt.% $K_2O$ leads to nearly stoichiometric specimens. This is established by studying the following properties; XRD patterns, temperature dependences of the phase transition temperature, energy of the fundamental absorption edge, the shape of the absorption band of the $OH^-$vibration and linewidths of the ESR of $Fe_{Li}^{3+}$.

Czochralski법으로 congruent(48.6mol% $Li_2O$)한 조성의 $LiNbO_3$와 congruent한 조성에 Fe2O3를 0.05mol%, congruent한 조성에 $K_2O$를 6wt%, congruent한 조성에$K_2O$$Fe_2O_3$를 각각 6wt%, 0.05mol% 첨가한 융액으로부터 $LiNbO_3$ 단결정을 c-축 방향으로 성장시켰다. 성장된 결정들은 편광 현미경과 Laue법에 의해 축을 결정한 후 절단하여 연마하였다. 시료들은 상온에서 XRD pattern을 측정하고 상온~$1230^{\circ}C$의 온도영역과 100Hz~13MHz의 주파수영역에서 유전율을 측정하였으며 상온에서 결정내 $Fe^{3+}$ 이온에 대한 ESR 스펙트럼과 UV-VIS, IR영역에서의 투과율을 측정하였다. Congruent한 조성에 $K_2O$를 6wt% 첨가한 융액으로부터 성장시킨 결정의 상온에서의 XRD pattern은 congruent한 조성의 결정과 거의 같으며 상전이온도(Tc)는 증가하고 $Fe^{3+}$을 첨가하면 ESR 스펙트럼은 세기가 증가하며 lineshape가 거의 대칭적으로 되고 선폭도 훨씬 줄어든다. 또 UV-스펙트럼의 흡수단은 단파장쪽으로 이동하며 OH- 이온에 대한 IR-흡수 스펙트럼은 2886nm 성분 스펙트럼이 현저하게 증가한다. 이 결과에 의하면 congruent한 조성에 $K_2O$를 6wt% 첨가한 융액으로부터 성장시킨 결정은 결정 내의 [Li]/[Nb]비가 1에 가까운 거의(nearly) stoichiometric한 결정이 되었음을 알수 있다.

Keywords

References

  1. J. Cryst. Growth v.119 S. Kan;M. Sakamoto;Y. Okano;K. Hoshikawa;T. Fukuda
  2. J. Cryst. Growth v.110 B.C. Grabmaier;W. Wersing;W. Koestler
  3. Appl. Phys. Lett. v.12 J.G. Bergman;A. Ashkin;A.A. Ballman;J.M. Dziedzic;H.J. Levinstein;R.G. Smith
  4. J. Cryst. Growth v.116 K. Kitamura;J.K. Yamamoto;N. Iyi;S. Kimura
  5. IEEE J. Quant. Elect. v.26 no.1 D.H. Jundt;M.M. Fejer;R.L. Byer
  6. Phys. Stat. Sol. v.(a)133 G.I. Malovichko;V.G. Grachev;L.P. Yurchenko;V.Ya. Proshko;E.P. Kokaanyan;V.T. Gabrielyan
  7. J. Phys. Chem. Solids v.56 no.9 G.I. Malovichko;O. Cerclir;J. Estienne;V. Gracher;E. Kokanyan;C. Boulesteix
  8. Current Topics in Material Science v.1 A. Rauber;E.Kaldis(Ed.)
  9. J. Cryst. Growth v.79 B.C. Grabmaier;F. Otto
  10. J. Appl. Phys. v.72 Y. Furukawa;M. Sato;K. Kitamura;Y. Yamima;M. Minakata
  11. J. Cryst. Growth v.110 S.C. Abrahams;P. Marsh
  12. J. Chem. Phys. v.56 G.E. Peterson;A. Carnezale
  13. J. Appl. Phys. v.69 no.11 L.J. Hu;Y.H. Chang;F.S. Yen
  14. J. Appl. Phys. v.71 no.2 P.F. Bordui;R.G. Norwood
  15. J. Appl. Phys. v.71 P.F. Bordui;R.G. Norwood;D.H. Jundt;M.M. Fejer
  16. Cryst. Res. Technol. v.19 I. F$\"{o}$ldv$\'{a}$ri;K. Polg$\'{a}$r;R. Voszka;R.N. Balasanyan
  17. Appl. Phys. Lett. v.70 no.21 L. Kov cs;G. Ruschhaupt;K. Polg$\'{a}$r;G. Corradi;M. W hlecke
  18. Solid State Comm. v.89 no.3 G.I. Malovichko;V.G. Grachev;O.F. Schirmer
  19. Solid State Comm. v.12 J.R. Herrington;B. Dischler;A. R uber;J. Schneider
  20. J. Phys. Chem. Solids v.52 no.6 L. Kov$\'{a}$cs;M. W$\"{o}$hlecke;A. Jovanovi$\'{c}$;K. Polg$\'{a}$r;S. Kapphan
  21. Sov. Phys. Sol. State v.28 G.I. Malovichko;V.G. Grachev;V.T. Gabrielyan;E.P. Kokanyan
  22. Electron Paramagnetic Resonance in Compounds of Transition Elements S.A. Altshuler;B.M. Kozyrev
  23. Radiat. Eff. Defects Solids v.119-121 C.R.A. Catlow;A.V. Chadwick;M. Cole;S.M. Tomlinson
  24. J. Phys: Codens. Matter v.4 H. Sothe;J.M. Spaeth