Abstract
The effect of quenching speed of melt-spinning on intrinsic coercivity ($_iH_c$$) of annealed ribbons and the crystallization behavior from amorphous $Nd_{14.73}Fe_{78.67}B_{6.60}$ alloy have been studied. We have found that the intrinsic coecivity for annealed melt-spun ribbon is reduced with increasing of quenching rate. $\alpha$-Fe and $Fe_3B$ were formed as intermediate phases prior to the formation of $Nd_2Fe_{14}B$ phase during crystallization. The $Fe_3B$ is disappeared with crystallization of $Nd_2Fe_{14}B$ phase. But the $\alpha$-Fe phase is retained in fully crystallized ribbon by annealing. The intrinsic coercivity loss of annealed ribbon with increasing of quenching speed is believed to be due to existence of soft magnetic phase $\alpha$-Fe in annealed ribbons.
과냉각된 melt-spun $Nd_{14.73}Fe_{78.67}B_{6.60}$리본의 급속응고속도 및 열처리에 따른 보자력의 변화를 조사하였으며, 이 결과를 분석하기 위하여 비정질로 부터의 결정화 거동을 연구하였다. 리본 제조시 급속응고속도가 증가함에 따라 결정화 후의 고유 보자력은 감소하였다. $Nd_{14.73}Fe_{78.67}B_{6.60}$ 비정질은 안정한 $Nd_2Fe_{14}B$ 상으로 결정화하는 과정에서 $\alpha$-Fe와 $Fe_3B$ 상이 생성된다. $Fe_3B$ 상은 $Nd_2Fe_{14}B$ 상이 결정화됨과 동시에 사라지나 $\alpha$-Fe 상은 완전히 결정화된 이후에도 기지상인 $Nd_2Fe_{14}B$ 상과 함께 잔류한다. 열처리된 리본내에 잔류하는 연자성상인 $\alpha$-Fe에 의해 고유 보자력의 특성이 저하하였다.