Synthesis of the BaTiO$_3$ Powders by the Glyscine-Nitrate Process and Its Properties (Part I)

Glycine-Nitrate 법에 의한 BaTiO$_3$ 분말의 합성 및 그 특성(Part I)

  • 박지애 (연세대학교 세라믹공학과) ;
  • 김구대 (한국과학기술연구원 세라믹공정센터) ;
  • 이홍림 (연세대학교 세라믹공학과) ;
  • 이동아 (한국과학기술연구원 세라믹공정센터)
  • Published : 1998.08.01

Abstract

The BaTiO3 powders extensively used as MLCC (Multilayer ceramic capacitor) in electronic ceramic in-dustry were synthesized by GNP (Glycine-Nitrate process) The powders were prepared using carbonate and alkoxide as starting materials and nitric acid was used as a solvent for starting materials as well as an oxidant for combustion. The BaTiO3 powders were synthesized using different amounts of glycine as a fuel for combustion. The characteristics of synthesized powders were examined with helium pycnometer X-ray diffraction(XRD) Brunauer-Emmett-Teller with N2 adsorption and scanning electron microscopy(SEM). It was found that single phase BaTiO3 could be formed when the as-synthesized powders were heat-treated at 100$0^{\circ}C$ When the glycine/cation molar ratio was 1,2 specific surface area was 24m2/g

MLCC(Multilayer ceramic capacitor) 등의 전자 세라믹스 분야에서 폭넓게 이용되는 BaTiO3 분말 제조를 위해 GNP(Glycine-Nitrate process)법을 이용하였다. 일반적인 GNP법과는 달리 출발물질로 카보네이트와 알콕사이드를 도입했고, 연소반응의 산화제 및 출발물질의 용매로써 질산을 사용하였으며, 연소합성시의 연료인 글리신의 첨가량을 달리하여 분말을 합성하였다. 연소합성된 분말의 특성은 helium pycnometer, XRD, N2 흡착을 이용한 BET, 주사전자현미경 등으로 분석하였다. 제조된 전구체 분말은 100$0^{\circ}C$로 하소시에 단일상의 BaTiO3 상으로 전이되었으며, 조성이 1.2인 경우 24m2/g의 높은 비표면적 값을 나타내었다.

Keywords

References

  1. J. Mater. Sci. v.25 Review: Low-temperature Synthesis and Processing of Electronic Materials in the BaO-T1O₂System P. P. Phule;S.H. Risbud
  2. J. Am. Ceram.Soc. v.42 no.5 Formation of BaTiO₃from BaCO₃and T1O₂in Air and in CO₂ L. K. Templeton;J. A. Pask
  3. J. Solid. State Chem. v.26 Thermal Decomposition of (BaT1) Citrates into Barium Titanate D. Hennings;W. Mayr
  4. Ceramic Powder Science II, Ceram. Trans. v.1 Synthesis and Properties of Stoichiometric Barium Titanate Powder Derived from a Catechol Precursor Complex N. J. Ali;S.J. Milne;G. L. Messing(et al.)
  5. Ceramic Powder Science IV, Ceram. Trans. v.22 Preparation of BaTiO₃Powder by Ultrasonic Spray Pyrolysis H. Cho, J. Lee;S. Park;G. L. Messing(et al.)
  6. Ceramic Powder Science IV, Ceram. Trans. v.22 Synthesis of SrTiO₃and BaTiO₃Powders by Spray Pyrolysis K. Nonaka;S. Hayashi;T. Yano;K. Okada;N. Otsuka;G. L. Messing(et al.)
  7. 한국요업학회지 v.33 no.4 수열법에 의한 PbTiO₃분말 합성 박병규;이태근;이기강
  8. 요업기술 v.10 no.2 Oxalate 법에 의한 Barium Titanate 분체 제조 신효순;이병교
  9. US Patent no.3 Method of Preparing Lead and Alkaline Earth Titanates and Niobates and Coating Method Using the Same to Form a Capacitor M. P. Pechini
  10. Mater. Lett. v.10 no.1;2 Glycine-Nitrate Combustion Synthesis of Oxide Ceramic Powders L. A. Chick; L. R. Pederson;G. D. Maupin;J. L. Bates;L. E. Thomas;G. L. Exarhos
  11. 한국요업학회지 v.34 no.10 Glycine-Nitrate Process를 이용하여 산화물 출발물질로부터 (La,Sr)MnO₃분말의 제조 김재동;문지웅;김구대;김창은
  12. 한국요업학회지 v.33 no.4 Self-Sustaining Combustion Process를 이용한 NiO/YSZ 초미세 복합분말 제조 김선재;정충환;김경호;김영석;국일현
  13. US Patent Method of Making Metal Oxide Ceramic Powers by Using a Combustible Amino Acid Compound L. R. Pederson(et al.)
  14. J. Am. Ceram. Soc. v.79 no.6 Effects of Temperature and Atmosphere on the Formation Mechanism of Barium Titanate Using the Citrate Process J. D. Tsay;T. T. Fang
  15. Am. Ceram. Soc. Bull. v.51 no.12 High Purity Reactive Alumina Powders : II, Particle Size and Agglomeration Study D. W. Johnson;D. J. Nitti;L. Berrin
  16. Ceramic Powder Science IV, Ceram. Trans. v.22 Processing Issues of Hydrothernal Synthesis of Fine Dielectric Powders W. J. Dawson;J. C. Preston;S. L. Swartz;G. L. Messing(et al.)