Abstract
We have studyed the surface electric resistiance for inner conductive film consisted of graphite and iron oxide by coating the conductive paint on inner face of 28" wide CRT funnel and have evaluated the working properties of 28" wide CRT according to the surface electric resistiance. We found that the viscosity of paint and the thickness of conductive film became the higher but the surface electric resistiance of con-ductive films was the lower than before in accordance with the increase of solid contents in conductive paint and that the surface condition and the surface electric resistiance of conductive films changed highly ac-cording to the drying conditions also. From these results we could get the uniform thickness and the un-iform film resistance and the optimum working property of selectric propertise in CRT when we used the conductive paint with solid contents 28% and viscosity about 13cps.
브라운관 funnel glass 내며의 흑연 피막의 저항에 관하여 연구하기 위하여 흑연이 함유된 도전성 도료를 제조하여 flow coating 방법으로 28" wide TV용 funnel glass 내면에 도포하고 흑연피막의 특성과 브라운관의 동작 특성을 평가하였다. 고형분 농도가 증가함에 따라 도전성 도료의 점도와 흑연피막의 두께는 증가하였으며 흑연피막의 전기저항은 감소하였다. 도포 후 건조조건에 따라서도 도전막의 표면상태, 전기저항 및 브라운관의 초기동작 특성등이 다르게 나타났다. 도전성 도료의 고형분 농도는 27%, 점도는 13 cps 전후에서 안정한 흑연피막을 제조할 수 있었으며, 이 때 진공특성이 최적의 상태로 나타났다. 그리고 도전성 도료의 상태와 제조조건에 따라서 브라운관의 다른 전지적 특성들도 변할 수 있기 때문에 브라운관 전체의 특성을 동시에 평가를 해야한다고 생각한다. 그리고 funnel glass에서의 부의 별 저항산포 차리를 줄이기 위해서는 도포 시에 도전성 도료를 주입하는 위치, 건조 조건, funnel glass의 예열 온도 등에 대한 조사도 이루어져야 한다고 생각한다.