Synthesis of Aluminum Sulfate from Kaolin and Its Thermal Decomposition

카올린으로부터 알루미늄황산염의 합성 및 열분해

  • Park, Seong-Su (Dept. of Inorganic Mat. Eng., Pusan National Univ.) ;
  • Gang, Hyo-Gyeong (Kyung Nam Center, Korea Institute of Industry and Technology Information) ;
  • Park, Hong-Chae (Dept. of Inorganic Mat. Eng., Pusan National Univ.) ;
  • Park, Hui-Chan (Dept. of Inorganic Mat. Eng., Pusan National Univ.)
  • 박성수 (부산대학교 무기재료공학과) ;
  • 강효경 (산업기술정보원 경남지역기술센터) ;
  • 박홍채 (부산대학교 무기재료공학과) ;
  • 박희찬 (부산대학교 무기재료공학과)
  • Published : 1998.02.01

Abstract

Aluminum sulfate, $AI_{2}(SO_4)_3\cdot18H_2O$ was prepared by adding of kaolin-dissolved sulphuric acid into ethanol and its thermal decomposition behavior was discussed. As-synthesized high purity precipitate particles were platelike shapes of $2\mu\textrm{m}$ size. With increasing drop rate of leach liquor into ethanol, the crystallite sizes of the precipitate decreased. The apparent activation energies for dehydration and sulfate decomposition of the precipitate were $11.9Kcal mol^{-1}$ and $48.2kcal mol^{-1}$ respectively.

카올린을 용해시킨 황산용액을 에탄올에 주입함으로써 알루미늄황산염의 침전물, $AI_{2}(SO_{4})_{3}\cdot18H_{2}O$을 제조하고, 그것의 열분해거동을 검토하였다. 합성된 고순도의 침전물은 약 $2\mu\textrm{m}$크기의 판상형태의 입자들로 구성되어져 있었다. 에탄올속으로 카올린을 용해시킨 황산용액의 주입속도를 증가시킴에 따라서 생성된 침전물의 결정사 크기는 감소하였다. 침전물의 탄수 및 탄황산에 대한 겉보기 활성화에너지는 각각 $11.9Kcal mol^{-1}$$48.2kcal mol^{-1}$ 이었다.

Keywords

References

  1. Adv. Ceram. Mat v.3 A. Roosen;H. Hausner
  2. J. Am. Ceram. Soc. Bull v.60 J. D. W. Johnson
  3. Am. Ceram. Soc. Bull v.63 J. E. Blendell;H. K. Bowen;R. L. Coble
  4. J. Appl. Chem. Biotechnol v.28 T. Sato;F. Ozawa;S. Ikoma
  5. J. Mat. Lett v.19 T. V. Mani;P. K. Pillai;A. D. Damodaran;K. G. K. Warrier
  6. J. Mat. Lett v.14 Z.Yu;Q.Zhao;Q.Zhang
  7. J. Am. Ceram. Soc v.48 J. L. Henry;H. J. Kelly
  8. J. Mater. Sci. Lett v.14 H. K. Kang;K. H. Kim;H. C. Park
  9. J. Am. Ceram. Soc v.77 H. K. Varma;T. V. Mani;A. D. Damodaran;K. G. Warrier
  10. J. Mat. Sci. Lett v.14 H. K. Kang;K. H. Kim;H.C. Park
  11. CRC handbook of chemistry and phyics(74th ed.) D. R. Lide
  12. Elements of X-ray Diffraction B. D. Cullity
  13. Collid Chemistry v.1 P. P. Von Weimarn;J. Alexander(ed.)
  14. Analy. Chem v.29 H. E. Kissinger
  15. J. Am. Ceram. Soc v.64 E. Kato;K. Daimon;M. Nanbu