Abstract
Effect of cold drawing ratio and aging time on the hardness of lnconel 718 wire aged at 11l6K were investi¬gated by hardness measurement and scanning & transmission electron microscopy. Hardness which was 245Hv in as¬solution treated condition increased very rapidly to 450Hv as cold drawing ratio increased to 50%. The hardness in the early stage of aging was increased by the precipitation of $\gamma^{'}$ and $\gamma^{'}$ phases and after the peak hardness, the hardness was decreased by the transformation of $\gamma^{'}$ phase to $\delta$ phase. The time to reach peak hardness during aging appeared to be reduced with the increase of cold drawing ratio, and those times were 30, 10, and 5 minutes for 0, 30 and 50% cold drawn materials, respectively. For the 50% cold drawn material. $\gamma^{'}$ and $\gamma^{'}$ were precipitated by aging for 5 minutes at 1116K. The hardness in the same material was largely decreased under the initial hardness by the recrystallization.
Inconel 719 선재의 경도에 미치는 냉간신선가공량과 시효시간의 영향을 경도측정과 전자현미경을 사용하여 조사하였다. 고용화처리된 재료의 경도는 245Hzv이었으나 50% 냉간신선가공으로 450Hv까지 증가했다. 경도값은 시효시간이 증가함에 따라 초기에 증가하다 감소하는 것으로 나타났으며, 시효 초기 경도증가는 $\gamma^{"}$과 $\gamma^{'}$ 상의 석출에 의한 것이며, 최고경도 이후의 경도감소는$\gamma^{'}$상이 $\delta$상으로 변태되었기 때문이다. 냉간가공도가 증가함에 따라 최고경도에 이르는 시간은 감소되어 0, 30, 50%가공재들에 대해 각각 30, 10, 5분으로 나타났다. 이는 냉간가공으로 인해 $\gamma^{'}$ / $\gamma^{'}$ 상의 석출이 촉진되었기 때문이다. 50%가공재의 경우 1116K에서 5분 시효로$\Upsilon^{'}$ 및 $\Upsilon^{'}$상들이 석출되었다. 또한 50%가공재에서는 초기경도 이하로 경도값이 감소되었는데, 이와 같은 경도값의 큰 감소는 재결정이 일어났기 때문이다.