전자빔 코팅 및 플라즈마 용사에 의한 안정화지르코니아/CoNiCrAlY 계면의 산화거동

Oxidation Behavior at the Interface between E-beam Coated $ZrO_{2}$-7wt.%$Y_{2}O}_{3}$and Plasma Sprayed CoNiCrAlY

  • Choi, Won-Seop (Division of Materials Science and Metallurgical Engineering, Hanyang University) ;
  • Kim, Young-Do (Division of Materials Science and Metallurgical Engineering, Hanyang University) ;
  • Jeon, Hyeong-Tag (Division of Materials Science and Metallurgical Engineering, Hanyang University) ;
  • Kim, Hyon-Tae (Korea Institute of Science and Technology) ;
  • Yoon, Kook-Han (Korea Institute of Science and Technology) ;
  • Hong, Kyung-Tae (Korea Institute of Science and Technology) ;
  • Park, Jong-Ku (Korea Institute of Science and Technology) ;
  • Park, Won-Sik (Korea Electric Research Institute)
  • 발행 : 1998.06.01

초록

열차폐코팅층의 박리는 세라믹/금속접합층 계면에서 취성이 큰 스피텔의 생성, 금속과 세라믹의 열팽창계수의 차이, 세라믹층의 상변태, 코팅층의 잔류응력에 기인한다. 본 연구에서는 인코넬 713C에 전자빔 코팅 및 플라즈마 용사법으로 코팅된 안정화지르코니아/CoNiCrAIY 계면의 산화거동을 조사하기 위하여 $900^{\circ}C$에서 등온산화시험동안 생성되는 산화막층과 스피넬 생성 거동을 관찰, 분석하였다. 코팅 직후 코팅층에 고르게 분포하고 있는 Co,Ni,Cr,AI,Zr의 원소들이 산화시간에 따라 확산하여 산화반응을 하였다. 초기 20시간의 산화기시간에 안정화지르코니아/CoNiCrAIY 계면에 주요 성분이 $\alpha$-$AI_2O_3$인 산화막층이 생성되었고, CoNiCrAIY층에는 AI의 외부확산으로 인한 AI 결핍지역이 생성되었다. 산화시험동안 $\alpha$-AI2O층이 임계두께까지 성장한 후에 산화막층의 성장속도는 감소하였고, 안정화지르코니아/산화막층 계면에 스피넬, $Cr_2O_3$, $CO_2CrO_4$의 형성으로 인한 크랙이 관찰되었다.

The spallation of a thermal barrier coating layer depends on the formation of brittle spinels. thermal expansion mismatch between ceramic and metal. the phase transformation of a ceramic layer and residual stress of coating layer. In this work. the formation mechanism of oxide scale formed by oxidation treatment at 90$0^{\circ}C$ was investigated in order to verify oxidation behavior at the interface between E-beam coated $Zr0_2$-7wt.% $Y_20_3$ and plasma sprayed CoNiCrAIY. Some elements distributed in the bond coating layer were selectively oxidized after oxidation. At the initial time of oxidation. AI-depletion zone and $\alpha$-$Al_O_3$,O, were formed at the bond coating layer by the AI-outward diffusion. After layer grew until critical thickness. spinels. $Cr_20$, and $C0_2CrO_4$ by outward diffusion of Co. Cr, Ni were formed. It was found that the formation of spinels may be related to the spallation of $Zr0_2$-7wt.% $Y_20_3$ during isothermal oxidation.

키워드

참고문헌

  1. Metallurgical and Ceramic Protective Coating Kurt. H. Stern
  2. Surface and Coating Technology v.54;55 F.Jamarani;R.W.Bertram
  3. Surface and Coating Technology v.39;40 J.R.Brandon;R.Taylor
  4. Surface and Coating Technology v.5 R.Taylor;J.R.Brandon;P.Morrell
  5. Oxidation of Metals v.26 no.5;6 K.L.Luthra;C.L.Briant
  6. Meterials and Processes for Surface and Interface Engineering Y.Pauleau
  7. 대한금속학회회보 v.10 no.1 최원섭,전형탁,김영도
  8. Adv. Ceram. Master. v.12 S.L.Shinde;I.E.Reimanis;L.C.Dejonghe
  9. Thin Solid Films v.95 R.A.Miller;E.Lowell
  10. Mater. Sci. and Eng. v.A111 B.C.Wu;E.Chang
  11. Mater. Sci. Technol. v.2 no.3 A.Bennett
  12. Thin Solid Films v.127 T.E.Strangman
  13. High Temperature Oxidation of Metals N.Birk;G.H.Meier
  14. Journal of Materials Science v.27 L.Lelait;S.Alperine;R.Mevrel
  15. Journal of American Ceramic Society v.72 B.C.Wu;E.Chang;F.F.Chang
  16. Journal of Materials Engineering and Performance v.3 no.1 Y.H.Sohn;R.R.Biederman;R.D.Sisson(Jr.)
  17. Mater Sci. Eng. v.A121 E.Y.Lee;R.R.Biederman;R.D.Sisson(Jr.)
  18. Surface and Coating Technology v.86;87 J.A.Haynes;E.D.Rigney;Mattison,K.
  19. Plasma Surf. Eng. v.1 E.Y.Lee;R.R.Biederman;R.D.Sisson(Jr.)
  20. NASA Contractor Report 189111 Thermal barrier coating life prediction model development S.M.Meier;D.M.Nissley;K.D.Sheffler
  21. Metallurgical Transactions v.3 I.A.Kvernes;P.Kofstad