석탄회 이용 인공제올라이트 제조시 바닷물 활용효과

Utilization of Seawater in the Production of Artificial Zeolite from Fly Ash

Sodium hydroxide concentrations were adjusted to 2.0, 2.5, 3.0 and 3.5M by dissolution in seawater. The fly ash was hydrothermally reacted with sodium hydroxide solutions (1:8, W:V) at $100^{\circ}C$ under the closed system. X-ray diffractogram proved that Na-P1 type zeolite was produced from bituminous coal fly ash. It is different from the X-ray of artificial zeolite produced by using sodium hydroxide solution dissolving in distilled water. Solid sieve structure was developed well by hydrothermal reaction with the ash and 3.0M sodium hydroxide. However chinks were observed in the structure of the product by 3.5M sodium hydroxide. CEC of the artificial zeolite was $244.5cmol^+\;kg^{-1}$ at 2.0M, 259.8 at 3.0M, 263.4 at 3.0M and 179.8 at 3.5M after 24 hours hydrothermal reaction; Artificial zeolite having high CEC, above $244.5cmol^+\;kg^{-1}$ could produce by using lower concentration of NaOH prepared in seawater than other production methods.