Engineering Properties of Permeable Polymer Concrete with Rice-Husk Ash

왕겨재를 혼입한 투수성 폴리머 콘크리트의 공학적 성질

This study was performed to evaluate the engineering properties of permeable polymer concrete with rice-husk ash. The following conclusions were drawn; 1. The highest sterngth was achieved by 50% filled rice husk-ash permeable polymer concrete, it was increased 24% by compresseve, 123% by tensile and 90% by bending strength than that of the normal cement concrete, respectively. 2. The static modulus of elasticity was in the range of $1.27{\times}10^5{\sim}1.75{\times}10^5kgf/cm^2$, which was approximately 58~70% of the normal cement concrete. The higher elastic modulus was showed by 50% filled rice-husk ash permeable polymer concrete, relatively. The poisson's number of permeable polymer concrete was less than that of the normal cement concrete. 3. The ultrasonic pulse velocity was in the range of 2,503~3,083m/sec, which was showed about the same compared to that of the normal cement concrete. The higher pulse velocity was showed by 50% filled rice-husk ash permeable polymer concrete. 4. The water permeability was in the range of $4.612{\sim}5.913{\ell}/cm^2/hr$, and it was largely dependent upon the mix design. These concrete can be used to the structures which need water permeability.

이 연구는 폴리머를 결합재로 사용하고 시멘트와 왕겨재를 충전재로 혼입한 투수용 폴리머 콘크리트의 공학적 성질을 구명한 것으로서, 이 연구를 통해 얻어진 결과를 요약하면 다음과 같다. 1. 각 강도는 시멘트와 왕겨재를 중량비로 반반씩 충전재로 사용한 투수용 폴리머 콘크리트에서 가장 크게 나타났고, 보통 시멘트 콘크리트보다 압축강도에서는 24%, 인장강도에서는 123%, 휨강도에서는 90%가 증가되었다. 2. 정탄성계수는 $1.27{\times}10^5{\sim}1.75{\times}10^5kgf/cm^2$으로 보통 시멘트 콘크리트의 58~70%정도로서 변형성이 크게 나타났으며, 충전재로는 시멘트와 왕겨재를 중량비로 반반씩 사용한 투수용 폴리머 콘크리트에서 가장 높은 값을 보였고 왕겨재의 혼입량이 많을수록 높은 값을 보였으며, 포아손수는 3.140~5.314로 보통 시멘트 콘크리트보다 작게 나타났다. 3. 초음파진동속도는 2,503~3,083m/sec로서 보통 시멘트 콘크리트와 거의 비슷하게 나타났으며, 시멘트와 왕겨재를 반반씩 충전재로 사용한 투수용 폴리머 콘크리트에서 비교적 높은 값을 보였다. 4. 투수량은 $4.612{\sim}5.913{\ell}/cm^2/hr$로서 배합설계에 따라 크게 좌우되었으며, 이러한 콘크리트는 투수를 요하는 구조물에 유용하게 이용할 수 있을 것이다.