A Study on the Microstructures of Rapidly Solidified Ti-($45{\sim}58at%$)Al Intermetallic Compound

급속응고된 TiAl 금속간화합물의 Al함량 변화에 따른 미세조직변화에 관한 연구

The microstructures of rapidly solidified binary Ti-Al alloys containing $45{\sim}58\;at%Al$ have been studied using C/S (carbon/sulfur), N/O (nitrogen/oxygen) analyser, X-ray fluorescence spectrometer (XRF), X-ray diffractometer (XRD), optical microscope (OM) and scanning electron microscope (SEM). The phases present in the alloys and their distribution were found to be a sensitive function of Al content. Essentially single-phase (${\gamma}$) microstructures were observed to alloys with 45 at%Al, 55 at%Al and 58 at%Al. In other content alloys, two phase (${\alpha}_2$, ${\gamma}$) microstructures were observed. The 48 at%Al, 52 at%Al alloys contain (${\gamma}+{\alpha}_2$) phase and ${\alpha}_2$ phase. These results indicate that rapid solidification affect the solidification path, then metastable phase forming during solidification.