Abstract
Optical filters utilizing the evanescent filed coupling between the side polished fiber and polymer planar waveguide were fabricated and optical properties of the devices were measured. A scheme for reducing polarization dependent properties of the device was proposed and demonstrated experimentally. Our measurement results showed that resonance wavelengths and filtering depth of the optical filters can be determined by adjusting thickness of planar waveguide and polishing depth of the fiber. The device fabrication procedure including fiber polishing steps and formation of polymer planar waveguide were described. The optical characteristics of fabricated optical filers were that 3 dB bandwidth was 15 nm, the resonance wavelength difference between the TE and TM polarized response was less then 2 nm, and insertion loss was less then 0.2 dB. The measured resonance wavelength drift dut to the variation of ambient temperature was -0.35 nm/$^{\circ}C$.
측면 연마된 단일모드 광섬유와 다중모드 폴리머 평면도파로 사이의 소산장 결합을 이용한 광필터를 제작하고 그 특성을 측정하였다. 소자의 편광의존성을 줄일 수 있는 방법 제안하였으며 실험으로 검증하였다. 그리고 광필터의 공진파장과 여과 깊이는 평면도파로의 두께와 연마깊이로서 적절히 선택할 수 있음을 실험으로 보였다. 광섬유 연마과정, 폴리머 평면도파로 제작 등을 포함한 소자제작 공정을 소개하였다. 제작된 광필터의 3㏈대역폭은 15nm, 삽입손실은 0.2㏈, 편광에 따른 공진 파장의 차이는 2nm 이하였다. 그리고 주위온도에 의한 공진파장의 이동거리는 -0.35nm/$^{\circ}C$로 측정되었다.