Abstract
Aluminum hydrates were synthesized using $AlCl_3$.$6H_2O$as starting material by precipitation method. The phases of obtained powder were amorphous, boehmite, bayerite, nordstrandite depending on the pH of solutions. Aluminum hydrates transformed to $\alpha-Al_2O_3$via $\gamma$- $Al_2O_3$,$\delta$- $Al_2O_3$,and $\theta$-$Al_2O_3$,and particle sizes were grown by increment of heating temperature. The TEX>$\gamma$- $Al_2O_3$ powder was coated on intermediate layer of ceramic membrane by the dip-coating method, and unsupported membrane was also prepared for comparison. The supported layer showed porous structure with small grains, but the unsupported layer revealed interconnected larger grains. Grain growth is dominant in the unsupported layer than in the supported one.
$AlCl_3{\cdot}6H_2O$를 출발원료로 침전법에 의해 알루미늄 수화물을 합성하였다. 용액의 pH에 따라 amorphous, boehimite, bayerite, nordstrandite 상을 얻었고, 수산화 알루미늄은 열처리 온도가 증가함에 따라 $\gamma$, $\delta$, $\theta$를 거쳐${\alpha}-Al_2O_3$로 전이되었으며, 입자크기도 증가하였다. ${\gamma}-Al_2O_3$ 를 담금피막법(dip-coating method)으로 중간층 위에 코팅하였고, 비교를 위해 비지지체 분리막도 준비하였다. 지지체 분리막은 작은 입자(grain)들로 구성된 다공질 구조(porous structure)를 나타내었지만, 비지지체 분리막에서는 상호 연결된 큰 입자(grain)들이 나타났다. 지지체 분리막에서 보다 비지지체 분리막에서 결정립 성장이 명백하게 나타났다.