Abstract
An experimental study for manufacturing lightweight aggregates from sewage sludge ash of sewage treatment facilities was carned out in senses of sludge disposal and utilization. In case of SA alone, aggregates with S.G. 1.67 was obtained at sintering temperature of $1250^{\circ}C$, and heating rate affects little to volume expansion rate and volume expansion rate was decreased more or less by heating time. In case of adding 10 wt% of RFCC to SA, lightweight aggregates with S.G. 1.07 was obtained and volume expansion rate was increased by heating time. The optimum adding amounts of RFCC to manufacture lightweight aggregates was 10wt% and the condition that shows maximum volume expansion rate was $20^{\circ}C/min$ of heating rate, $1250^{\circ}C$ of sintering temperature and 50 mmutes of heating time. According to adding amounts of RFCC, Compressive strength of sample results in 30 wt% RFCC>SA>20 wt% RFCC>10 wt% RFCC.
생활하수처리장에서 발생하는 슬러지연소재(SA)에 정유공장의 폐촉매(RFCC)를 첨가시켜 제조하려는 실험.연구를 행하였다. SA만의 경우에는 $1250^{\circ}C$에서 열처리하였을 때 비중이 1.67인 골재를 얻을 수 있었으며, 부피팽창률은 승온속도에 큰 영향이 없었고 소성시간에 따라서는 다소 저하하는 경향을 보였다. SA에 RFCC를 10 wt% 첨가한 경우에 $1250^{\circ}C$에서 비중이 1.07인 경량골재를 얻을 수 있었으며 소성시간에 따라 부피팽창율이 다소 증가하였다. 경량골재를 제조하기 위한 최적 RFCC 첨가량은 10 wt%이었으며 최대 부피팽창율을 보인 조건은 승온속도; $20^{\circ}C/min$, 소성온도; $1250^{\circ}C$, 유지시간; 50분의 경우였다. RFCC의 첨가량에 따라 제조된 시편의 압축강도는 30 wt% RFCC>SA>20 wt% RFCC>10 wt% RFCC의 경향을 보였다.