Abstract
Corrosion behavior of austenitic stainless steels of SUS 316L and SUS304L in molten salt of LiCl and $LiCl/Li_2O$ has been investigated in the temperature range of $650~850^{\circ}C$. Corrosion products of SUS316L and 304L in hot molten salt consisted of two layers-an outer layer of Li(CrFe)$O_2$and an inner layer of$Cr_2O_3$. The corrosion layer was uniform in molten salt of LiCl, but the intergranular corrosion occurred in addition to the uniform corrosion in mixed molten salt of LiCl/$Li_2O$. The corrosion rate increased slowly with the increase of temperature up to $750^{\circ}C$, but above $750^{\circ}C$ rapid increase in corrosion rate observed. SUS316L stainless steel showed slower corrosion rate than SUS 304L, exhibiting higher corrosion resistance in the molten salt.
LiCl 및 $LiCl/Li_2O$ 용융염분위기에서 오스테나이트 스테인레스강, SUS 316L과 SUS 304L의 부식특성을 650~$850^{\circ}C$ 온도범위에서 조사하였다. SUS 316L과 304L의 부식층은 외부 $Li(CrFe)O_2와 내부 Cr_2O_3$의 2층 구조를 형성하였다. LiCl 용융염중에서는 균일한 부식충이 형성되지만, $LiCl/Li_2O$ 혼합용융염중에서는 균일한 부식충 형성외에 업계부식이 발생되는 것을 알 수 있었다. $750^{\circ}C$까지 온도 증가에 따른 부식속도의 증가속도는 느리고, $750^{\circ}C$ 이상에서는 부식속도가 급격히 증가하였다. 용융염분위기에서 SUS 316L은 SUS 304L에 비하여 부식속도가 느려셔 보다 좋은 내식성을 나타내였다.