Electromagetic Wave Absorbing Properties of $Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$(X=Cu, Mg, Mn)-Rubber Composite

$Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$(X=Cu, Mg, Mn)-Rubber Composite의 전파흡수특성에 관한 연구

Electromagnetic wave asorbing properties of the $Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$, where X was replaced by substitution elements Cu, Mg, Mn, have been studied. The structure, shape, size and magnetic properties of the $Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$ were analyzed by XRD, SEM, VSM. The relative complex permittivity, permeability, and electromagnetic wave absorbing properties were measured by Network Analyzer. The structure, shape, size and magnetization value of the $Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$ were found to be similar in spite of substitution elements. The coercive force and hysteresis-loss showed maximum value when Mg was substituted for X. The dielectric loss(${\varepsilon}_r"/{\varepsilon}_r'$) was found to be maximum value when Mn was substituted for X. Also the magnetic loss(${\mu}_r"/{\mu}_r'$} was found to be maximum with Cu substitution. The electromagnetica wave absorbing property of the $Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$-Rubber composite with 4mm thickness was excellent as over - 40dB at 9GHz, and the $Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$-Rubber composite with 8mm thickness was over-40dB at 2GHz. Those composites also showed superior microwave absorbing properties.

$Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$의 조성에서 X를 각각 Cu, Mg, Mn으로 치환시켜 치환원소에 따른 결정구조와 형상, 입도 및 자기적 성질을 비교 분석하여고, Network Analyzer을 이용하여 $Ni_{0.5}-Zn_{0.4}-X_{0.1}{\cdot}Fe_2O_4$-Rubber Composite의 재료정수 및 전파흡수특성에 대하여 비교 조사하였다. 치환원소에 관계없이 동일한 결정구조와 형상 및 입도를 나타냈고, VSM 분석결과 치환원소에 관계없이 동일한 자화값을 가지며, Mg로 치환된 경우 가장 큰 보자력과 자기이력손실을 나타냈다. 또한 Mn으로 치환된 경우 가장 높은 유전손실(${\varepsilon}_r"/{\varepsilon}_r'$)을, Cu로 치환된 경우에는 가장 큰 자기손실(${\mu}_r"/{\mu}_r'$)을 나타냈다. 4mm의 두께로 제조한 Compos-Composite에서는 Mg로 치환된 시료가 2GHz에서 -40dB이상의 가장 우수한 전파흡수특성을 나타내었다.