An Experimental Study on the Engineering Properties Of Rice-Straw Ash Concrete

볏짚재를 혼입(混入)한 콘크리트의 공학적(工學的) 특성(特性)에 관한 실험적(實驗的) 연구(硏究)

This study is performed to evaluate the engineering properties of rice-straw ash concrete using normal portland cement, natural aggregates and rice-straw ash. The following conclusion are drawn; 1. The dynamic modulus of elasticity is in the range of $289{\times}10^3{\sim}345{\times}10^3kgf/cm^2$, which is showed about the same compared to that of the normal cement concrete. The highest dynamic modulus is showed by 5% rice-straw ash filled rice-straw ash concrete 2. The static modulus of elasticity is in the range of $268{\times}10^3{\sim}335{\times}10^3kgf/cm^2$, which is showed about the same compared to that of the normal cement concrete. The dynamic modulus is increased approximately 3~10% than that of the static modulus. 3. The poisson's number of rice-straw ash concrete is less than that of the normal cement concrete. 4. Accordingly, if we use suitable quantity of rice-straw ash as a replacement of cement, it will greatly improve engineering properties of concrete.

이 연구는 보통 포틀랜드 시멘트와 천연골재 및 볏짚재를 혼입한 콘크리트의 공학적 특성을 실험적으로 구명한 것으로서, 이 연구를 통해 얻어진 결과는 요약하면 다음과 같다. 1. 볏짚재 콘크리트의 동탄성계수는 $289{\times}10^3{\sim}345{\times}10^3kgf/cm^2$ 정도로 보통 시멘트 콘크리트의 91~108%로써 보통 시멘트 콘크리트와 유사하게 나타났으며, 볏짚재를 5% 혼입한 콘크리트에서 가장 크게 나타났다. 2. 볏짚재 콘크리트의 정탄성계수는 $268{\times}10^3{\sim}335{\times}10^3kgf/cm^2$ 정도로 보통 시멘트 콘크리트와 유사하게 나타났고, 볏짚재를 5% 혼입한 콘크리트에서 가장 크게 나타났다. 3. 볏짚재 콘크리트의 푸아송수는 4.235~6.604의 범위로 보통 시멘트 콘크리트보다 대체적으로 작게 나타났다. 4. 적정량의 볏짚재를 혼입하여 콘크리트를 제조할 경우, 볏짚재 콘크리트의 공학적 특성이 보통 시멘트 콘크리트보다 우수할 뿐만 아니라, 농업부산물의 활용으로 인한 경제적 측면서도 많은 기여를 할 수 있을 것으로 기대된다.