Effect of TEA on Acceleration Shotcrete
숏크리트용 급결제에 미치는 트리에탄올아민의 영향
- Chun, Yong-Jin (Department of New Material & Applied Chemistry, Chungwoon University) ;
- Cho, Suk-Hyeong (Department of Hi-Technology Material & Applied Chemistry, Hyejeon College) ;
- Hong, Young-Ho (Department of Hi-Technology Material & Applied Chemistry, Hyejeon College) ;
- Lee, Gun-Jik (Insung Powdertech Co. Ltd.)
- Received : 1999.06.09
- Accepted : 1999.11.11
- Published : 1999.12.10
Abstract
In this study the effect of organic additive, triethanolamine(TEA), and temperature change of accelerator for shotcrete was studied. Then the amount of accelerator, temperature and W/C were experimentally investigated. Effects of hydration time and hydration heat of concrete on organic additive amount were analysed by DSC, SEM and XRD. We found that the hydration heat was increased and hydration time was decreased with TEA(<5 wt %). The order of hydration rate of potassium accelerator was PA < PC-3 < PC-5 < PC-8.
숏크리트용 급결제의 작용매커니즘을 규명하고 온도변화에 따른 급결제의 영향을 실험적으로 밝히고자 수행된 본 연구에서는 급결제의 양, 급결제시 온도, W/C의 양등에 대한 수화시간 및 수화열을 DSC로 분석하였으며, 그에 따른 압축강도 분석과 SEM, XRD분석으로 급결제와 콘크리트 사이에서 일어나는 물리 화학적 현상을 고찰하였다. 급결제의 첨가량이 증가할수록 수화반응 시간이 빨라지고, 같은 양의 급결제를 넣었을 때 첨가제인 TEA가 많이 들어간 급결제 일수록 수화시간이 빨라지며, 수화열도 증가하였다. 그러나 TEA가 5% 이상인 경우에는 더 이상 수화열의 증가는 없었다. 온도가 증가할수록 수화열은 짧은 시간에 발생하고, 급결제 양의 증가에 따라서도 수화열은 빠르게 발생하였다. P type의 경우 TEA가 많이 첨가된 PA < PC-3 < PC-5 < PC-8의 순으로 온도에 따른 수화 반응이 빠르게 진행되었다. TEA를 첨가하지 않은 콘크리트의 압축강도가 높은 경향을 나타내었으며, 양생일수가 증가할수록 압축강도는 증가하는 경향을 보였다.