A Study on Corrosion Failure of a Weathering Steel Weldment with Various Applied Potentials in Acid-chloride Solution

산-염소이온 분위기의 인자전위에 따른 내후성강 용접부의 부식파괴에 관한 연구

  • Published : 2000.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

The stress corrosion cracking(SCC) and hydrogen embrittlement cracking(HEC) characteristics of a weathering steel weldment were investigated in aerated acid-chloride solution. The electrochemical properties of weldment were investigated by polarization test and galvanic corrosion test. Weathering steel did not show passive behavior in the acid-chloride solution. Galvanic corrosion between the weld metal and the base metal was not observed because the base metal was anodic to the weld metal. The slow-strain-rate tests(SSRT0 were conducted at a constant strain rate o 7.87×{TEX}$10^{-7}${/TEX}/s at corrosion potential, and at potentiostatically controlled anodic and cathodic potentials. The weldment of weathering steel was susceptible to both anodic dissolution SCC and hydrogen evolution HEC.

Keywords

References

  1. National cooperative highway research program report 272 Performance of weathering steel in bridges P. Albrecht;A. H. Naeemi
  2. Application note for unpainted weathering steel structures v.PCP No. 95-1 POSCO
  3. Corrosion v.52 no.12 Modeling of Atomspheric Corrosion Behavior of Weathering Steel in Sulfur Dioxide-Polluted Atmospheres J.H. Wang;F.I. Wei, H. C. Shih
  4. Corrosion v.26 no.10 Electrochemical Reduction of Thick Rust Layers Formed on Steel Surfaces H. Okada;Y. Hosoi
  5. Corrosion v.44 no.7 Infrared Spectroscopic Analysis of Phase Trnasformation Processes in Rust Layers Formed on Weathering Steels in Bridge Spans A. Raman;B. Kuban
  6. Corrosion v.50 no.7 Structures of Rust on Weathering Steel in Rural and Industrial Environments H.E. Townsend;T.C. Simpson
  7. Welding J. v.53 T.G. Gooch
  8. 대한금속학회지 v.34 no.12 Cu-25at%Au 단결성의 입내응력부식균열에 관한 연구 이재봉
  9. J. of Testing and Evaluation v.1 no.2 Metallurgical Aspects of the Failure of the Point Pleasant Bridge J.A. Bennet;H. Mindlin
  10. NACE NACE Standard TM0177-96
  11. 대한용접학회지 v.15 no.5 산성비 분위기에서 교량용 강재 SWS400의 용접부 부식에 관한 연구 정원석;김정구;서창제;이병훈
  12. Welding Metallurgy, 4th Ed. v.1 G.M. Linnert
  13. Handbook on Corrosion Testing and Evaluation S.W. Dean
  14. 한국부식학회지 v.22 no.4 HY-130강의 응력부식균열에 미치는 인가전위와 미세구조의 영향 김준식;권혁상;김규영;이성근;심인옥;김영우
  15. Corrosion v.55 no.9 Hydrogen Permeation Through Protected Steel in Open Seawater and Marine Mud J. Benson;R.G.J. Edyvean
  16. Corrosion v.28 no.7 Cathodic Protection and Hydrogen in Stress Corrosion Cracking C.F. Barth;A.R. Troiano
  17. Corrosion v.53 no.5 Stress Corrosion Cracking of Fe₃Al and Fe-16%Al Alloys J.G. Kim;R.A. Buchanan
  18. Metals Handbook, 9th Ed. v.13 Stress-corrosion cracking R.H. Jones
  19. Metals Handbook,9th Ed. v.13 Hydrogen Damage Bruce Craid
  20. 대한금속학회지 v.35 no.8 고온·고압 환경하에서 정전위법에 의한 인코넬합금의 입계응력부식 저항성 평가 맹완영;남태운