Abstract
The influence of $O_2$partial presure on saturation magnetization, coercivity and effective permeability(0.5~100MHz) of as-deposited Fe-Sm-O thin films, which were fabricated by RF magnetron reactive sputtering method, were investigated. The nanocrystalline Fe(sub)83.4Sm(sub)3.4O(sub)13.2 thin film fabricated at $O_2$partial pressure of 5% exhibits the best magnetic softness with saturation magnetization of 18kG, coercivity of 0.82 Oe and effective permeability about 2,600 at 0.5~100MHz. $\alpha$-Fe grain size is decreased with increasing $O_2$partial pressure. In case of $O_2$partial pressure of 10%, it is observed that FeO compound is formed and soft magnetic properties are decreased. The electrical resistivity of Fe-Sm-O thin films were increased with increasing $O_2$partial pressure, the electrical resistivity of Fe(sub)83.4Sm(sub)3.4O(sub)13.2 thin film with the best soft magnetic properties was 130 $\mu$$\Omega$cm. Therefore, It is assumed that the good soft magnetic properties of Fe(sub)83.4Sm(sub)3.4O(sub)13.2 thin film results from high electrical resistivity and decreasing $\alpha$-Fe grain size due to precipitation of Sm-Oxide phase.
RF magnetron sputtering법으로 초미세결정 Fe-Sm-O계의 박막을 상온에서 제작하여 산소분압에 따른 포화자화, 보자력, 고주파에서의 투자율(100MHz)을 조사하였다. 최적조건인 5%의 산소분압에서 제조한 초미세결정 Fe(sub)83.4Sm(sub)3.4O(sub)13.2박막은 포화자속밀도 18kG, 보자력 0.82 Oe, 실효투자율 (0.5~100MHz) 2,600 이상의 우수한 연자성을 나타내었다. 산소분압이 증가함에 따라 $\alpha$-Fe 결정립의 크기가 감소하여 10%이상의 산소분압에서는 FeO가 생성되어 연자기적 성질이 열화되었다. Fe-Sm-O계 박막의 전기비저항은 산소분압이 증가함에 따라 증가하는 경향을 나타내었으며 우수한 연자기적 성질을 가지는 Fe(sub)83.4Sm(sub)3.4O(sub)13.2박막의 경우, 전기비저항은 130 $\mu$$\Omega$cm이었다. 따라서 미세하게 형성된 $\alpha$-Fe 결정립과 높은 전기비저항 때문에 초미세결정 Fe(sub)83.4Sm(sub)3.4O(sub)13.2박막이 고주파에서 우수한 연자기적 성질을 가지는 것으로 판단된다.