Abstract
The dielectric properties of complex perovskite ($Pb_{1-x}Ca_{x}$)($Fe_{0.5}Ta_{0.5}$)$O_{3}$ with >($0.5{\le}x{\ge}0.65$ were investigated at microwave frequencies. Dilectric constant decreased with increasing Ca content, and was directly proportional to the cube of average ionic ra야 of A-site. For the specimen of x=0.6 sintered at $1250^{\circ}C$ for 3 h in air, dielectric constant (k) of 63, QF of 11000 GHz, and the temperature coefficient of resonant frequency(TCF) of -14ppm/$^{\circ}C$ were obtained. As Ca content increased, TCF of the specimen negatively increased due to the reduction of the tolerance factor(t). Changes in intrinsic loss with varying Ca content was investigated by the infrared reflectivity spectra ranging 50 to 4000 $cm^{-1}$, which were calculated by the Kramers-Kronig analysis and classical oscillator model. The relative tendency of microwave dielectric properties of the ($Pb_{1-x}Ca_{x}$)($Fe_{0.5}Ta_{0.5}$)$O_{3}$ specimens calculated from the reflectivity data were in good agreement with the results by the post resonant method.
마이크로파 대역에서 복합 페롬스타이트 ($Pb_{1-x}Ca_{x}$)($Fe_{0.5}Ta_{0.5}$)$O_{3}$($0.5{\le}x{\ge}0.65$) 세라믹스의 마이크로파 유전 특성에 대하여 고찰하였다. Ca 양이 증가할수록 유전 상수는 감소하였고, 유전 상수는 A-site 이온 평균 반경의 세제곱에 비례하였다. x=0.6일때 공기중에서 $1250^{\circ}C$ 3시간 소결시 유전율은 63, QF는 11000GHz 및 공진주파수의 온도계수(TCF)는 -14 $ppm/^{\circ}C$을 갖는 마이크로파 유전체를 얻을 수 있었다. Ca양이 증가함에 따라 tolerance factor 가 감소하여 TCF는 음의 방향으로 증가하였다. Ca 조성 변화에 따른 고유한 우전 손실 변화물 50 $cm^{-1}$~4000$cm^{-1}$범위에서 원적의선 반사율을 측정하고, Kramers-Kronig 분석과 고전 조화 진동자 모델(classical oscillator model)을 사용하여 분석하였다. 반사율 곡선으로부터 계산한 ($Pb_{1-x}Ca_{x}$)($Fe_{0.5}Ta_{0.5}$)$O_{3}$ 세라믹스의 마이크로파 유전특성 값은 측정한 유전특성 값의 경향과 잘 일치하였다.