Abstract
Silica slab wavegudie was fabricated on Si substrates by FHD for planar optical passive devices. The slab waveguide consists of lower clad and core layers, where core layer index is controlled by GeO2 addition. Doping of GeO2 in silica is difficult because of the low deposition density due to nonspherical particle generation in FHD process. Silica core particles deposited at various conditions such as flame temperature and substrate scanning were analyzed by SEM and TEM. As the flame temperature increased, the surface roughness of the core layer was decreased up to 3.6 nm after consolidation. Index difference and thickness of core of slab waveguide were 0.3%, 8$\mu\textrm{m}$ respectively. Measured optical loss at TE mode was <0.04 dB/cm at 1.3$\mu\textrm{m}$ and <0.06 dB/cm at 1.55$\mu\textrm{m}$.