Biaxial Fracture Behavior of Alumina Ceramics : Indentation Effect on Ball-on-3-ball Test

압입에 따른 알루미나 세라믹스의 이축 파괴 거동

  • 정성민 (연세대학교 세라믹공학과) ;
  • 박성은 (연세대학교 세라믹공학과) ;
  • 이홍림 (연세대학교 세라믹공학과)
  • Published : 2000.07.01
Download PDF
⟨ Previous Next ⟩

Abstract

The biaxial fracture behavior of alumina ceramics was studied using ball-on-3-ball test. The polished surfaces of alumina specimens were indented at 0mm, 1mm, 2mm, 3mm apart from the center of the specimen along path A, passing between the two supporting balls from the center of the specimen, and along path B, passing above the three supporting balls from the center of the specimen. The fracture strength of the indented specimens was measured using the ball-on-3-ball test, a kind of biaxial strength test. The fracture strength increased with increasing the distance from the center to indented position. The fracture strength of the specimen indented along path B was higher than that of the specimens indented along path A. It was presented that the fracture caused by tangential stress rather than radial stress when the indented positions are 1mm and 2mm from the center of the specimen. This phenomenon was in good agreement with FEM analysis.

Keywords

References

  1. Strength and Fracture of Glass and Ceramics J. Mencik
  2. Ceram. Bull. v.59 no.5 An Improved Biaxial Flexure Test for Ceramics D. B. Marshall
  3. 요업학회지 v.36 no.3 Ball-on-3-ball 시험에서 이축 강도의 결정 박성은;이중현;이홍림
  4. ASTM Annual Book of Standards v.15.02 ASTM Standard F394-78. American Society for testing and Materials
  5. Int. Journ. of Fracture v.13 no.1 Some Approximate Treatments of Fracture Statistics for Polyaxial Tension International Journal of Fracture S. B. Batdorf
  6. J. Am. Ceram. Soc. v.61 no.7-8 A General Approach for the Statistical Analysis of Multiaxial Fracture A. G. Evans
  7. J. Am, Ceram.. Soc. v.73 no.8 Ceramics Reliability : Statistical Analysis of Multiaxial Failure Using the Weibull Approach and the Multiaxial Elemental Strength Model J. Lamon
  8. J. Am. Ceram. Soc. v.73 no.7 Equivalence of Physically Based Statistical Fracture Theories for Reliability Analysis of Ceramics in Multiaxial Loading L. Chao;D. K. Shetty
  9. J. Am. Ceram. Soc. v.74 no.2 Reliability Analysis of Structural Ceramics Subjected to Biaxial Flexure L. Chao;D. K. Shetty
  10. J. Am. Ceram. Soc. v.62 no.9-10 Biaxial and Uniaxial Data for Statistical Comparisons of a Ceramic's Strength M. N. Giovan;G. Sines
  11. J. Am. Ceram. Soc. v.64 no.1 Biaxial Fracture Studies of a Glass-Ceramics D. K. Shetty;A. R. Rosenfield;G. K. Bansal;W. H. Duckworth
  12. Ceram. Bull. v.59 no.12 Biaxial Flexure Tests for Ceramics D. K. Shetty;A. R. Rosenfield;P. McGuire;G. K. Bansal;W. H. Duckworth
  13. 요업학회지 v.34 no.10 알루미나 세라믹스의 동적피로거동 이홍림;이규형;박성은
  14. J. Mater. Res. v.12 no.2 Falure Behavior of Alumina and Alumina/silicon Carbide Nanocomposites with Natural and Artificial Flaws F. Meschke;P. Alves-Riccardo;G. A. Schneider;N. Claussen
  15. J. Am. Ceram. Soc v.63 no.9-10 Flaw Characteristics in Dynamic Fatigue: The Influence of Residual Contact Stresses D. B. Marshall;B. R. Lawn
  16. ANSYS-Engineering Analysis System User's Manual A. J. Swanson
  17. Strength and Fracture of Glass and Ceramics J. Men k
  18. Engineering Properties of Steel P. D. Harvey
  19. Proceedings of the Sixth International Fatigue Congress v.2 A Finite Element Study of Conditions for Early Crack Growth at Inclusions in Contact Fatigue A. Melander