Abstract
TiO$_2$thin films were prepared on the glass by a conventional spin coating method with $TiO_2$ sol(30wt%, anatase). The thickness of the thin films were controlled by the number of coating cycles: one cycle is composed of spin coating, drying, and heating process. The reaction rate of the film was obtained by the photodecomposition of gaseous benzene under 0.44 and 2.0mW/$\textrm{cm}^2$ UV light on the film surface. For an incident UV light intensity of 0.44mW/$\textrm{cm}^2$, the reaction rate was increased with the thickness of the film, caused by extent of surface area, but there was no change over the thickness of about 4$\mu\textrm{m}$. The porous $TiO_2$ thin film has comparatively vast effective surface area, which under relatively high-intensity UV illumination causes the reaction rate to be controlled by the film thickness.
$TiO_2$sol(30wt%, anatase)을 이용하여 스핀코팅으로 유리기판에 $TiO_2$박막을 제조하였다. 박막의 두께는 코팅주기의 횟수가 조절하였다. 한 코팅주기는 스핀코팅, 건조, 열처리를 포함한다. 박막의 반응성은 막 위에서의 자외선강도가 0.44와 2.mW/$\textrm{cm}^2$인 조건에서 벤젠기체의 광분해 속도를 통해 조사하였다. 박막의 두께가 증가할수록 표면적으로 증가로 인해 반응성은 증가하였으며, 0.44mW/$\textrm{cm}^2$일 때 4$\mu\textrm{m}$정도 이상의 두께에서 반응성은 더 이상 증가되지 않았다. porous한 $TiO_2$박막은 비교적 넓은 유효표면적을 가지고 있으며, 그것은 비교적 높은 자외선 강도하에서 박막두께에 따라 반응속도를 증가시키는 결과를 낳았다.