Abstract
By the mechanical alloying method. Ni-WC composite materials were prepared to improve the deformation-resistance for creep and sintering of Ni-anode at the operating temperature of $650^{\circ}C$. Mechanically alloyed powder w was initially fabricated by ball milling for 80hr, and then amorphization was occurred by the destruction of ordered crystals based on XRD analysis. In order to investigate the electrochemical performance and sheet characteristics of Ni-WC anode, tape casting process was adopted. Finally, the obtained sheet thickness of Ni- we after sintering at $1180^{\circ}C$ for 60 minutes in $H_2$ atmosphere was O.9mm and the average pore size was $3~5{\mu\textrm{m}}$ with porosities of 55%. The second phase was not observed in Ni- W matrix while W particles were finely and uniformly distributed in Ni matrix. This fine and uniform distributed W particles in Ni matrix are expected to enhance the mechanical properties of Ni anode through the dispersion and solid solution hardening mechanisms.
MCFC 작동온도인 $650^{\circ}C$에서 음극의 creep과 소결에 의한 구조적 변형을 막기 위해 기계적 합금법에 의한 Ni-WC분말을 합금화하여 변형에 대한 저항성을 증대시키고자 하였다. 80시간동안 어트리션 밀링을 실시한 분말은 XRD 분석결과 결정규칙이 파괴된 비정질 상을 보였다. 제조된 분말은 적당한 점도의 슬러리로 제조후 테이프 캐스팅법에 의해 green sheet를 제조하였다. 제조된 박판의 두께는 0.9mm였고, 평균 기공 크기는 $3~5{\mu\textrm{m}}$, 기공율은 55%였다. 소결체의 XRD 분석결과 2차성은 생성되지 않았으며, SEM 및 dot-Mapping image를 통해 Ni matrix 안에 W 입자가 미세하고 균일하게 분포되어 있어 고용강화 및 분산강화를 통해 Ni 음극의 기계적 특성을 향상시킬 것으로 기대된다.