초록
The microstructure and electrical properties of ZnO-Pr$_{6}$/O$_{11}$-CoO-Er$_{2}$/O$_{3}$ based varistors were investigated with Er$_{2}$/O$_{3}$ additive content of the range 0.0 to 2.0 mol%. Most of the added Er$_{2}$/O$_{3}$ were segregated at the nodal points and grain boundaries and it coexisted with Pr$_{6}$/O$_{11}$ in the bulk intergranular layer. The average grain size was decreased in the range of 7.44 to 5.62${\mu}{\textrm}{m}$ at 130$0^{\circ}C$ and 18.36 to 9.11 at 135$0^{\circ}C$ with increasing Er$_{2}$/O sub 3/ additive content. The density of ceramics was in the range 4.87 to 5.08 g/cm$^3$ at 130$0^{\circ}C$ and 5.35 to 5.62 g/cm$^3$at 135$0^{\circ}C$. At 130$0^{\circ}C$ the varistors without Er$_{2}$/O$_{3}$ exhibited 29.66 in the nonlinear exponent and 28.23 $\mu$A in the leakage current whereas the varistors with 0.5 mol% Er$_{2}$/O$_{3}$ exhibited a high nonlinearity which is 52.78 in thenonlinear exhibited and 9.75 $\mu$A in the leakage current. At 135$0^{\circ}C$ the varistors without Er$_{2}$/O$_{3}$ exhibited a very poor nonlinearity indicating 2.08 in the nonlinear exponent and 133.79 $\mu$A in the leakage current whereas the varistors with 1.0mol% Er$_{2}$/O$_{3}$ exhibited a relatively high nonlinearity which is 36.79 in the nonlinear exponent and 5.92 $\mu$A in the leakage current. Therefore Er$_{2}$/O$_{3}$ was additive which greatly improve the nonlinearity. It is believed that ZnO-0.5 mol% Pr$_{6}$/O$_{11}$-1.0 mol% CoO-0.5 mol% Er$_{2}$/O$_{3}$ based ceramicss will be usefully used as a basic composition to develop the advanced pr$_{6}$/O$_{11}$-based ZnO varistors.ristors.ristors.