The Electric Properties of SrTiO$_3$Varistor Prepared by Co-precipitation Process

공침법으로 제초한 SrTiO$_3$바리스터의 전기적 특성

The low-voltage driven $SrTiO_3$ceramic varistor device was fabricated from $SrTiO_3$ powders prepared by co-precipitation method with $CuO-SiO_2$additives. Compare with conventional process, this process has advantages such as the reduction of the sintering temperature of $SrTiO_3$ ceramics by 100-$150^{\circ}C$ and the simplification of processing procedure. The non-linear coefficient value ($\alpha$) of the varistor showed 8.47 when it was sintered at $1350^{\circ}C$ for 2 h with 5 wt% additives in reducing atmosphere of 5% $H_2/N_2$ mixed gas. The low-voltage driven $SrTiO_3$ceramic varistor was obtained which has a breakdown voltage as low as 7 V.

공침법을 이용하여 제조한 $SrTiO_3$분말에 $CuO-SiO_2$첨가물을 혼합하여 저전압구동형 SrTiO$_3$세라믹 바리스터 소자를 제조하였다. $CuO-SiO_2$첨가물을 이용한 $SrTiO_3$세라믹 바리스터제조 공정은 복잡한 공정을 단순화시킬 수 있을 뿐만 아니라, 일반적인 소결온도보다 100~$150^{\circ}C$ 낮은 온도에서도 소결이 되었다. 이 바리스터의 비직선계수($\alpha$) 값은 첨가물 5 wt% 혼합하여 $1350^{\circ}C$에서 하소한 시편에서 8.47의 최고값을 나타냈으며, 이때의 구동전압은 7 V 이하로 낮은 구동전압을 가진 바리스터를 제조할 수 있었다.