Abstract
The crystallographic and magnetic properties of the sample F $e_{0.8}$ $Co_{0.18}$(BN)$_{0.02}$ synthesized by microwave arc-melting with the maximum power of 3.5 kW have been studied by the methods of an X-ray diffraction and the measurement of the magnetic hysteresis using the vibrating sample magnetometer at room temperature. The samples were prepared in a form of pellet pressed under the pressure of 9,000 N/c $m^2$, rolled coldly, and treated with the different temperatures. The X-ray diffraction pattern of pelleted sample shows that the crystal structure of the sample is bcc as same as that of Fe with a good uniformity. The X-ray diffraction pattern shows that a residual stress, which exists in the sample, is eliminated by final 90$0^{\circ}C$ annealing. As rolling rate and heat treatment temperature increases, the saturation magnetization and the remanence of the samples increase whereas the coercivity of the samples shows decrease. Also the saturation magnetization and the remanence of the samples were affected by rolling rate and rolling direction than heat treatment temperature, but the coercivity of the samples was affected by rolling rate and direction as well as heat treatment temperature. This means that a domain wall motion is easy due to elimination of a residual stress and an inclusion which exists in the sample by rolling and heat treatment and a local induced-magnetization easy axis was also formed to parallel to the rolling direction due to creation of the like-atom pairs across the slip plane by rolling......
F $e_{0.8}$ $Co_{0.18}$(BN)$_{0.02}$의 구조와 자기적성질은 최대출력 3.5 kW인 고주파에 의한 아르곤 플라즈마 분위기에서 제작되었고, 제작된 시료는 상온에서의 X선 회절과 진동시료자력계를 이용한 자기이력곡선 측정 방법에 의해서 조사하였다. 시료는 수압기로 9,000 N/$cm^3$기 압력을 가하여 알약형태 제작하여 열처리와 가공처리를 네단계로 수행하였다. 첫 번째 단계에 의해서 준비된 시료의 X선 회절결과는 결정구조는 균질이며 각 시료는 동일한 결정구조를 갖는 단일결정상(single crystal phase)이며. 최종 900 $^{\circ}C$ 열처리를 통해서 시료내부에 존재하는 잔류응력이 제거된다. 롤링율과 열처리온도를 증가함으로써, 포화자화와 잔류자화는 증가하고, 보자력은 감소하는 한다. 잔류자화는 열처리에 의한 효과보다는 롤링율 과 방향에 의해서 변화의 폭이 크다. 또한 보자력은 롤링율과 방향 뿐만 아니라 열처리온도에 의해서도 영향을 받는다. 이 결과로서 롤링과 열처리효과에 의해서 시료내부에 존재하는 개재물과 잔류음력이 제거되어 자벽이동이 용이해졌음을 의미하며, 또한 롤링에 의해서 동족원자쌍 생성되어 롤링방향에 평행한 국부 유도자화용이축이 생성되었음을 의미한다.다.다.